Preparation method of dicyandiamide resin tanning agent

A technology of dicyandiamide and resin, which is applied in the field of preparation of dicyandiamide resin tanning agent, can solve the problems that cannot meet the national environmental protection, human body and environmental hazards, and achieve good napping effect, strong filling effect, and reduced formaldehyde content Effect

Inactive Publication Date: 2017-12-29
南通双狮化工有限公司
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Dicyandiamide resin tanning agent, also known as resin tanning agent R6, can effectively solve the problem of loose surface of crust leather, improve the grain surface of finished leather, make the leather body of finished leather smoother, the grain surface more fine, and the finished leather plump. Soft and elastic, after the treatment, the leather will be softened and uniform grains can be obtained; however, the dihydroamine resin tanning agent will add formaldehyde during the preparation process, and if there is no follow-up treatment, there will be some floating particles in the product Formaldehyde cannot meet the national environmental protection requirements, and at the same time, it will cause harm to the human body and the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of dicyandiamide resin tanning agent
  • Preparation method of dicyandiamide resin tanning agent
  • Preparation method of dicyandiamide resin tanning agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A kind of preparation method of dicyandiamide resin tanning agent, completes the preparation of dicyandiamide resin tanning agent through preparation sodium bisulfite solution, condensation reaction and drying step; Concrete steps are as follows:

[0018] (1) Prepare ammonium bisulfite solution: add 80Kg of water to the dissolution kettle, start stirring, then add 50Kg of sodium bisulfite, and stir until completely dissolved;

[0019] (2) Condensation reaction: Transfer the above-prepared sodium bisulfite solution into the condensation kettle, start stirring, add 80Kg of formaldehyde, then add 80Kg of dicyandiamide from the manhole, raise the temperature in the kettle to 75°C, and Insulate the reaction at high temperature for 2 hours. After the reaction, add 40Kg of urea from the manhole, and keep the reaction at 75°C for 1h. After the reaction, the temperature in the lower kettle is lowered to 60°C, and add 170Kg of water and 130-Kg of sulfurous acid from the manhole. ...

Embodiment 2

[0022] A kind of preparation method of dicyandiamide resin tanning agent, completes the preparation of dicyandiamide resin tanning agent through preparation sodium bisulfite solution, condensation reaction and drying step; Concrete steps are as follows:

[0023] (1) Prepare ammonium bisulfite solution: add 100Kg of water to the dissolution kettle, start stirring, then add 60Kg of sodium bisulfite, and stir until completely dissolved;

[0024] (2) Condensation reaction: transfer the above-prepared sodium bisulfite solution into the condensation kettle, start stirring, add 90Kg of formaldehyde, then add 100Kg of dicyandiamide from the manhole, raise the temperature in the kettle to 80°C, and Keep the reaction at high temperature for 4 hours. After the reaction, add 45Kg of urea from the manhole, and keep the temperature at 80°C for 3h. After the reaction, the temperature in the lowering kettle is lowered to 60°C, and add 190Kg of water and 150Kg of sodium bisulfite from the manho...

Embodiment 3

[0027] A kind of preparation method of dicyandiamide resin tanning agent, completes the preparation of dicyandiamide resin tanning agent through preparation sodium bisulfite solution, condensation reaction and drying step; Concrete steps are as follows:

[0028] (1) Prepare ammonium bisulfite solution: add 90Kg of water to the dissolution kettle, start stirring, then add 56Kg of sodium bisulfite, and stir until completely dissolved;

[0029] (2) Condensation reaction: Transfer the above-prepared sodium bisulfite solution into the condensation kettle, start stirring, add 86Kg of formaldehyde, then add 90Kg of dicyandiamide from the manhole, raise the temperature in the kettle to 77°C, and Insulate the reaction at high temperature for 3 hours. After the reaction, add 43Kg urea from the manhole, and keep the temperature at 77°C for 2h. After the reaction, the temperature in the lowering kettle drops to 60°C, and add 180Kg water and 140Kg sodium bisulfite from the manhole. , react...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a dicyandiamide resin tanning agent. The dicyandiamide resin tanning agent is prepared through steps of preparation of a sodium hydrogen sulfite solution, a condensation reaction and drying. The dicyandiamide resin tanning agent has the advantages as follows: the preparation technology of the resin tanning agent is improved, so that the prepared resin tanning agent has high filling performance, has an extremely high filling effect on soft parts of leather and has a good napping effect; excessive ammonium sulfite is added during condensation to react with free formaldehyde in materials, thus, the content of free formaldehyde in the product is reduced, and the product is more environmentally friendly.

Description

technical field [0001] The invention belongs to the technical field of leather chemical synthesis, and in particular relates to a preparation method of a dicyandiamide resin tanning agent. Background technique [0002] In recent years, retanning has shown its important role in the whole process of tanning, and is known as the "golden touch" in modern tanning industry technology. Retanning is the tanning of crust leather that has been main tanned. There are many kinds of retanning agents. Common organic retanning agents include natural retanning agents, resin tanning agents, synthetic tanning agents and aldehyde tanning agents. Playing a role in tanning, there are more and more types of retanning agents on the market, with rapid development and more diversified performance. [0003] Dicyandiamide resin tanning agent, also known as resin tanning agent R6, can effectively solve the problem of loose surface of crust leather, improve the grain surface of finished leather, make ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G12/16C08J11/02
CPCC08G12/16C08J11/02C08J2361/22
Inventor 孙桂龙王启军丛慧云
Owner 南通双狮化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com