A kind of solar heat reflection thermal insulation coating structure and preparation method thereof

A technology of thermal insulation and solar heat, applied in the direction of reflective/signal paint, coating, filling slurry, etc., can solve the problem of anti-crack mortar air permeability, high weather resistance requirements, poor adhesion of the wall base, thermal insulation The problem of unsatisfactory board application, etc., achieves the effect of excellent heat reflection cooling and thermal insulation effect, saving refrigeration cost, and good batch scraping construction.

Active Publication Date: 2019-03-22
CHINA NAT OFFSHORE OIL CORP +3
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing thermal insulation boards made of thermal insulation materials with a combustion performance above Class A are not ideal in the application of external thermal insulation projects. They generally have poor adhesion to the base layer of the wall, and it is difficult to control the flatness during large-scale construction. The corners of the rear board are easy to protrude, and the anti-cracking mortar has high air permeability and weather resistance requirements, and poor thermal insulation performance, which brings inconvenience to the construction and high cost, which is inconsistent with the concept of energy saving and environmental protection.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of solar heat reflection thermal insulation coating structure and preparation method thereof
  • A kind of solar heat reflection thermal insulation coating structure and preparation method thereof
  • A kind of solar heat reflection thermal insulation coating structure and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0037] Such as figure 2 Shown, the preparation method of solar heat reflection thermal insulation coating structure among the present invention, comprises the following steps:

[0038] S101. Mix the mortar powder and water to prepare an inorganic thermal insulation mortar, scrape the inorganic thermal insulation mortar on the outer surface of the wall, dry and solidify to form an inorganic thermal insulation mortar layer 1;

[0039] S102. Mix the putty powder and water to prepare a flexible thermal insulation putty, scrape the flexible thermal insulation putty on the surface of the inorganic thermal insulation mortar layer 1 for trimming and leveling, and form a flexible thermal insulation putty layer 2;

[0040] S103. Mix the components of the elastic thermal insulation coating and spray it on the surface of the flexible thermal insulation putty layer 2, and form the elastic thermal insulation coating 3 after drying and curing;

[0041] S104. Brush or roll coat the components...

Embodiment 1

[0048] Preparation of solar heat reflective thermal insulation coating structure T-01

[0049] 1.1. Material preparation

[0050] 1.11. Preparation of inorganic thermal insulation mortar: weigh each component of the mortar powder according to the following weight percentages: cement 55%, floating beads 5%, vitrified microspheres 30%, wollastonite powder 6%, redispersible latex powder 3 %, 0.3% polypropylene fiber, 0.3% hydroxypropyl methyl cellulose ether, and 0.4% wood fiber. Stir and mix the above components with a disperser to form a mortar powder. Before construction, mix water and mortar powder according to The weight ratio of 8:10 is stirred evenly and stored for later use.

[0051] Among them, the cement is 42.5 grade ordinary Portland cement from Chongqing Conch Cement Co., Ltd., the floating beads are from Jiangsu Zhenjiang Blue Ribbon Thermal Insulation Material Factory, the vitrified microbeads are from Henan Xinyang Zhengda New Material Co., Ltd., and the wollasto...

Embodiment 2

[0064] Preparation of solar heat reflective thermal insulation coating structure T-02

[0065] 2.1. Material preparation

[0066] 2.11. Preparation of inorganic thermal insulation mortar: weigh each component of the mortar powder according to the following weight percentages: cement 50%, sepiolite 6%, vitrified microbeads 30%, wollastonite powder 8%, redispersible latex powder 5%, polypropylene fiber 0.2%, hydroxypropyl methyl cellulose ether 0.3%, wood fiber 0.5%, use a disperser to mix the above components evenly to form a mortar powder, mix water and mortar powder before construction Stir and mix evenly according to the weight ratio of 7:10, save it for later use.

[0067] Among them, the cement is 42.5 grade ordinary Portland cement from Chongqing Conch Cement Co., Ltd., the vitrified microbeads come from Henan Xinyang Zhengda New Material Co., Ltd., the wollastonite powder comes from Guangde Zhengyuan Wollastonite Powder Co., Ltd., and the redispersible latex The powder...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a solar heat reflection type heat insulation coating structure. The solar heat reflection type heat insulation coating structure comprises an inorganic heat insulation mortar layer, a flexible heat insulation putty layer, an elastic heat insulation coating and a solar heat reflection coating layer which are sequentially arranged at the outer surface of a wall body from interior to exterior. The solar heat reflection type heat insulation coating structure has the advantages that the cost is low, the bonding with the wall body is tight, the construction is simple and controllable, the excellent heat reflection cooling and heat insulation effects are realized, the combustion property class requirement is met, and the energy-saving and environment-protection concept is met.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a solar heat reflection and thermal insulation coating structure and a preparation method thereof. Background technique [0002] In the existing technology, the thermal insulation of building exterior walls is generally achieved by pasting insulation boards on the surface of the exterior walls. However, the once mature technology of pasting organic insulation boards on the market has been approved by the Ministry of Public Security because the material cannot achieve Class A combustion performance. "Document No. 65" is strictly prohibited to be used on the outer surface of civil buildings. Therefore, the insulation boards currently used are generally made of insulation materials with a combustion performance above Class A. However, the existing thermal insulation boards made of thermal insulation materials with a combustion performance above Class A are not ideal in the applicat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/52C04B28/04C09D133/00C09D5/33C09D7/61C09D7/63C09D7/65C09D5/34
CPCC04B28/04C04B41/009C04B41/52C04B2111/00482C08K2201/014C08L2205/02C08L2205/03C09D5/004C09D5/34C09D7/61C09D7/63C09D7/65C09D133/00C08L33/02C08L83/04C08K13/02C08K2003/2241C08K3/34C08K5/053C04B41/5079C04B41/5035C04B41/4596C04B41/5041C04B41/4857C04B41/5014C04B18/08C04B14/18C04B14/043C04B2103/0057C04B16/0633C04B24/38C04B18/26C04B14/08C04B14/06C04B24/383C04B28/00
Inventor 蔡青青史立平何庆迪戚剑孔志元
Owner CHINA NAT OFFSHORE OIL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com