A kind of antibacterial pa66/abs composite material and preparation method thereof

A technology of composite materials and antibacterial agents, which is applied in the field of antibacterial nylon composite materials and its preparation, can solve problems such as poor heat resistance, easy decomposition, and application limitations, and achieve the effects of ensuring sterilization efficiency, avoiding high-temperature oxidation, and expanding processing bandwidth

Active Publication Date: 2019-05-03
ZHUZHOU TIMES NEW MATERIALS TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The above existing patents all use organic antibacterial agent and inorganic antibacterial agent compound antibacterial system, which has achieved good antibacterial effect, but the PA content contained in the system is small, and the material has excellent wear resistance, self-lubrication and surface matte effect, etc. Poor aspects, resulting in limited application in some fields
In addition, because the organic antibacterial agent in the compound antibacterial system has problems such as poor heat resistance, short life, easy to decompose, and difficult to degrade, it is not conducive to the promotion in the PA66 / ABS alloy system with high PA66 content.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of antibacterial pa66/abs composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-3

[0037] The antibacterial PA66 / ABS composite material of three embodiments of the present invention shown in the formula of Table 1, the antibacterial PA66 / ABS composite material is mainly obtained by blending and melting the components shown in the following Table 1:

[0038] Table 1: PA66 / ABS composite material formulation

[0039] components

Example 1

Example 2

Example 3

Comparative example 1

Comparative example 2

Comparative example 3

PA66

50

60

70

50

60

70

processing activator

15

20

25

15

20

/

ABS

50

40

30

50

40

30

Compatibilizer

5

5

5

5

5

5

Toughener

15

15

12

15

/

12

Diffuser oil

0.1

0.2

0.2

0.1

0.2

0.2

Antibacterial agents

0.8

1.1

1.5

/

1.1

1.5

antioxidant

0.3

0.3

0.3

0.3

0.3

0.3

[0040] The processing activator used in the above example...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
viscosityaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to an antibacterial PA66 / ABS composite material. The antibacterial PA66 / ABS composite material is mainly prepared through blending the following ingredients in parts by mass and carrying out melting: 50-70 parts of polyhexamethylene adipamide, 10-30 parts of processing activator, 30-50 parts of acrylonitrile-butadiene-styrene, 5-10 parts of compatibilizer, 5-20 parts of toughener, 0.1-0.3 part of diffusion oil, 0.6-1.5 parts of antibacterial agent and 0.2-2 parts of auxiliaries. The antibacterial PA66 / ABS composite material is prepared through firstly, thoroughly mixing weighed polyhexamethylene adipamide, weighed processing activator, weighed acrylonitrile-butadiene-styrene, weighed compatibilizer and weighed diffusion oil in a high-speed mixer, then, adding the antibacterial agent and the auxiliaries into the mixture, and finally, adding the toughener into the mixture and carrying out thorough mixing, so as to obtain a premix; carrying out melt extrusion on the premix through a twin-screw extruder, and carrying out drawing, cooling and pelleting. The product provided by the invention has the advantages of easiness in processing, high antibacterial performance, excellent mechanical properties, and the like.

Description

technical field [0001] The invention belongs to the technical field of thermoplastic engineering plastics and its preparation, and in particular relates to an antibacterial nylon composite material and a preparation method thereof. Background technique [0002] Polyhexamethylene adipamide, commonly known as nylon 66 (PA66), is a thermoplastic engineering plastic widely used in automobiles, electronics, machinery and other fields. It has excellent wear resistance, impact resistance and self-lubricating properties. It is resistant to chemicals, but it is not resistant to strong alkali, and has high water absorption and creep. These shortcomings limit its application to a large extent. The PA66 / ABS composite material prepared by blending and modifying PA66 with acrylonitrile-butadiene-styrene (ABS) not only has the wear resistance, impact resistance and self-lubricating properties of nylon, but also has the toughness of ABS And rigidity, in addition to better surface matte eff...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L77/06C08L55/02C08L77/00C08L51/00C08L51/04C08L83/04C08K13/06C08K5/134C08K5/526C08K9/12C08K3/08
CPCC08L55/02C08L77/06C08L2205/02C08L2205/035C08L77/00C08L51/003C08L51/04C08L83/04C08K13/06C08K5/1345C08K5/526C08K9/12C08K2003/0806
Inventor 李雄武李方军黄彩霞朱志勇王雄刚
Owner ZHUZHOU TIMES NEW MATERIALS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products