A formability and magnesium alloy technology, applied in the field of metal material processing, can solve the problems of poor formability and high processing cost of magnesium alloys, and achieve the effect of improving the formability of processing
Inactive Publication Date: 2016-08-24
CHONGQING UNIV
View PDF7 Cites 6 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0005] The purpose of the present invention is mainly to provide a magnesium alloy with high formability for the problems of poor formability and high processing cost of existing magnesium alloys
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0017] In this embodiment, the magnesium alloy is composed of the following components by mass percentage: Zn0.5%, Ce0.2%, Ca0.2%, unavoidable impurities are about 0.015%, and the rest is Mg.
Embodiment 2
[0019] In this embodiment, the magnesium alloy consists of the following components in terms of mass percentage: 1.0% Zn, 0.2% Ce, 0.2% Ca, about 0.015% of unavoidable impurities, and the rest is Mg.
Embodiment 3
[0021] In this embodiment, the magnesium alloy consists of the following components by mass percentage: Zn 1.5%, Ce 0.2%, Ca 0.2%, unavoidable impurities about 0.015%, and the rest being Mg.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| density | aaaaa | aaaaa |
Login to View More
Abstract
The invention discloses high-formability magnesium alloy, comprising the following components according to percent by weight: 0.5-2.0% of Zn, 0.1-0.3% of Ce, 0.1-0.3% of Ca, < / =0.015% of unavoidable impurity and the balance of Mg, and preferably, also comprising 0.01-0.3% by weight of Mn. With weak texture, the magnesium alloy provided herein may bear great stress and high stress rate without cracking during extrusion, rolling and other plastic deformations, and processing formability of the magnesium alloy is effectively improved.
Description
technical field [0001] The invention belongs to the field of metal material processing, and in particular relates to a magnesium alloy with high formability. Background technique [0002] Magnesium alloy has high specific strength, specific stiffness, good damping, machinability and thermal conductivity, strong electromagnetic shielding ability, easy recycling, regeneration and many other excellent properties, making it widely used in aerospace, automobile industry, electronics industry The application in the fields of national economy and national defense is expanding day by day. And magnesium is the lightest metal structure material, with a density of only 1.74g / cm3, which is 2 / 3 of aluminum and 1 / 4 of steel. The wide application of magnesium alloy in industry will have a positive effect on energy saving and emission reduction. Therefore, magnesium alloy is known as "the green engineering material of the 21st century". [0003] Traditional magnesium alloys such as Mg-Al ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): C22C23/04C22C1/03C22F1/06
CPCC22C23/04C22C1/03C22F1/06
Inventor 潘复生黄光胜王冠刚黄伦韩廷状
Owner CHONGQING UNIV
Features
- Generate Ideas
- Intellectual Property
- Life Sciences
- Materials
- Tech Scout
Why Patsnap Eureka
- Unparalleled Data Quality
- Higher Quality Content
- 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com