A kind of preparation method of spotted glaze

A spot glaze and bottom glaze technology, which is applied in the field of ceramic manufacturing, can solve problems such as easy to absorb dirt, not suitable for daily tea sets, rough surface of spots, etc.

Active Publication Date: 2018-02-09
JIANGSU GAOCHUN CERAMICS
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The above-mentioned prior art belongs to the technical field of crystalline glaze, and its characteristic is that the spots are crystallized when the glaze surface is fired at high temperature. The surface of the spots is rough and dull. Although there is a certain artistic effect, the dull spots are easy to absorb dirt and are not easy to clean , not suitable as a daily tea set

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Base glaze raw materials: 20 parts of feldspar, 5 parts of Suzhou soil, 22 parts of quartz, 6 parts of dolomite, 7 parts of talc, 6 parts of titanium dioxide, 20 parts of frit, 5 parts of ZnO, Fe 2 o 3 For 8 parts, prepare the bottom glaze;

[0028] Surface glaze raw materials: 42 parts of feldspar, 15 parts of calcite, 4 parts of frit, 16 parts of quartz, 6 parts of Suzhou soil, 12 parts of earth bone, Fe 2 o 3 2 parts for spodumene and 1.5 parts for spodumene. The above-mentioned parts are all parts by weight.

[0029] Preparation of bottom glaze glaze slurry: mix raw materials: water: ball (weight ratio) in a ratio of 1:1:1.5, and ball mill through a ball mill. 1.5-1.6g / cm 3 ;The preparation of surface glaze raw materials used in the preparation process of surface glaze slurry, ball milling and glaze slurry fineness is the same as that of bottom glaze, and the specific gravity of glaze slurry is 1.4-1.50g / cm 3 .

[0030] Apply the bottom glaze slurry on the ce...

Embodiment 2

[0034] Base glaze raw materials: 18 parts of feldspar, 6 parts of Suzhou soil, 25 parts of quartz, 8 parts of dolomite, 5 parts of talc, 4 parts of titanium dioxide, 18 parts of frit, 6 parts of ZnO, Fe 2 o 3 For 7 parts, prepare the bottom glaze;

[0035] Surface glaze raw materials: 40.5 parts of feldspar, 13 parts of calcite, 6 parts of frit, 18 parts of quartz, 7 parts of Suzhou soil, 10.5 parts of earth bone, Fe 2 o 3 2.5 parts for spodumene and 2 parts for spodumene. The above-mentioned parts are all parts by weight.

[0036] Preparation of bottom glaze glaze slurry: mix raw materials: water: ball (weight ratio) in a ratio of 1:1:1.5, and ball mill through a ball mill. 1.5-1.6g / cm 3 ;The preparation of surface glaze raw materials used in the preparation process of surface glaze slurry, ball milling and glaze slurry fineness is the same as that of bottom glaze, and the specific gravity of glaze slurry is 1.4-1.50g / cm 3 .

[0037] Apply the bottom glaze slurry on the ...

Embodiment 3

[0041] Base glaze raw materials: 24 parts of feldspar, 6.5 parts of Suzhou soil, 20 parts of quartz, 5 parts of dolomite, 9 parts of talc, 5 parts of titanium dioxide, 17 parts of frit, 7 parts of ZnO, Fe 2 o 3 6.5 parts, prepare the bottom glaze;

[0042] Surface glaze raw materials: 44 parts of feldspar, 16.5 parts of calcite, 3.5 parts of frit, 17 parts of quartz, 5 parts of Suzhou soil, 14 parts of earth bone, Fe 2 o 3 1.8 parts for spodumene and 2.5 parts for spodumene. The above-mentioned parts are all parts by weight.

[0043] Preparation of bottom glaze glaze slurry: mix raw materials: water: ball (weight ratio) in a ratio of 1:1:1.5, and ball mill through a ball mill. 1.5-1.6g / cm 3 ;The preparation of surface glaze raw materials used in the preparation process of surface glaze slurry, ball milling and glaze slurry fineness is the same as that of bottom glaze, and the specific gravity of glaze slurry is 1.4-1.50g / cm 3 .

[0044] Apply the bottom glaze slurry on ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of speckled glaze.According to the preparation method, prepared ground glaze and cover glaze are adopted, ground glaze components start to be subjected to phase splitting at the melting temperature of 1150 DEG C-1180 DEG C in an oxidizing atmosphere by adopting a specific firing system to form a calcium-enriched and iron-poor phase and an iron-enriched and calcium-less phase which contain the different ingredients, then the ground gaze and the upper-layer cover glaze are penetrated each other at the melting temperature of 1250 DEG C-1280 DEG C, and after cooling is performed, the eel back speckled glaze is formed.According to the speckled glaze, the surface is smooth, the background ground glaze and speckles both have the vitreous luster, the lead dissolving-out amount and the cadmium dissolving-out amount in the product are both not detected out, and the speckled glaze can be used for tea tasting tea sets and daily tableware decorates.

Description

technical field [0001] The invention relates to a method for preparing spotted glaze, which belongs to the technical field of ceramic manufacturing. Background technique [0002] In the prior art, there have been introductions about spotted glazes. For example, CN201510037226.3 discloses a erythema crystalline glaze and a ceramic preparation method using the glaze. The glaze is mainly composed of the following raw materials in parts by weight: albite 20- 40 parts, 10-20 parts of quartz, 10-20 parts of calcite, 1-10 parts of calcite, 10-25 parts of ashes, 1-10 parts of glass powder, 5-15 parts of barium carbonate, 5-2 parts of iron oxide; preparation Methods: (1) Weigh the raw materials, wet grind them to get the glaze slurry and then stale; (2) Apply glaze on the biscuit body and carry out drying treatment; (3) Put the dried body in a kiln and fire it in 230-655 minutes Complete the entire firing process of heating-high-temperature heat preservation-cooling-low temperature ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/89C03C8/02
CPCC03C8/02C04B41/52C04B41/89C04B41/504C04B41/5022
Inventor 韩小伟刘志斌陈春明
Owner JIANGSU GAOCHUN CERAMICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com