Copper rod complete-synthesis coarse-drawing lubricating fluid and preparation method as well as use method thereof

A fully synthetic, large wire drawing technology, applied in the lubricating cooling fluid for machining and its preparation, the copper rod and copper rod fully synthetic large wire drawing lubricating fluid, the preparation field, can solve the problems of poor lubrication effect, short service period and high price , to achieve the effect of good protection, long service life and environmental protection

Inactive Publication Date: 2016-05-25
JIANGSU ZHONGMEI CABLE
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the defects existing in the prior art, the present invention provides a fully synthetic large wire drawing lubricant for copper rods, which solves the problems of poor lubricating effect, slow cooling, short service life, non-environmental protection and high price of existing wire drawing lubricants

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] The copper bar copper rod of the present embodiment fully synthesizes large wire drawing lubricating liquid, and lubricating liquid comprises the following components by weight: 1 part of copper protector, 5 parts of hydrophilic nonionic emulsifier (fatty acid soap and fatty acid alcohol amide mixed emulsifier ), 30 parts of water-based extreme pressure lubricant, 2 parts of borate ester, 3.5 parts of triethanolamine, 5 parts of dicarboxylate-based compound rust inhibitor, 3 parts of monobutyl ether coupling agent, 1 part of anti-hard water agent, 0.01 part Defoamer, 20 parts of distilled water;

[0018] The water-based extreme pressure lubricant comprises 20 parts of triethanolamine, 6 parts of dimer acid, 8 parts of ricinoleic acid polyester, 6 parts of caprylic acid and the distilled water of 2 times of triethanolamine;

[0019] The preparation method of the fully synthetic large wire drawing lubricating liquid for copper rods and copper rods of the present embodimen...

Embodiment 2

[0024] The copper rod copper rod of the present embodiment fully synthesizes large wire drawing lubricating liquid, and lubricating liquid comprises the following components by weight: 0.5 parts of copper protective agent, 3 parts of hydrophilic nonionic emulsifiers, 20 parts of water-based extreme pressure lubricants, 1 part Parts of boric acid, 2 parts of triethanolamine, 5 parts of dicarboxylate-based compound rust inhibitor, 2 parts of monobutyl ether coupling agent, 0.5 part of anti-hard water agent, 0.01 part of defoamer, 20 parts of distilled water;

[0025] The water-based extreme pressure lubricant comprises 20 parts of triethanolamine, 6 parts of dimer acid, 8 parts of ricinoleic acid polyester, 6 parts of caprylic acid and distilled water of 2 times the number of triethanolamine;

[0026] The preparation method of the fully synthetic large wire drawing lubricating liquid for copper rods and copper rods of the present embodiment comprises the following steps:

[0027...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses copper rod complete-synthesis coarse-drawing lubricating fluid and a preparation method as well as a use method thereof. The copper rod complete-synthesis coarse-drawing lubricating fluid is prepared from the following components in parts by weight: 0.5-1 part of copper protectant, 3-5 parts of mixed emulsifier, 20-40 parts of water-based extreme pressure lubricant, 1-2 parts of boric acid, 2-5 parts of cholamine, 2-5 parts of monobutyl ether coupler, 0.5-1 part of hard water resistor, 0.01-0.1 part of defoamer, 0.01-0.1 part of triethanolamine borate antirust agent and 20-25 parts of distilled water; the copper rod complete-synthesis coarse-drawing lubricating fluid is used by being diluted with water according to a ratio of 1:5-20. The copper rod complete-synthesis coarse-drawing lubricating fluid has the advantages that the lubricating property, cooling property and oxidation resistance can be matched with cleaning property for a long term, stableness is achieved, and the service cycle is long.

Description

technical field [0001] The invention relates to a lubricating cooling liquid for mechanical processing and a preparation method thereof, in particular to a copper rod and copper rod full-synthetic large-drawing lubricating liquid, a preparation method and a use method thereof, which belong to the technical field of chemical preparation. Background technique [0002] At present, the copper drawing used in the cable industry is to draw the copper rod with a diameter of 8.0mm through several molds to the required monofilament. A large amount of heat is released during the drawing of copper rods, and lubricants are used for lubrication and cooling. At present, the most used lubricants are mainly oily or non-synthetic lubricants. [0003] The current drawing liquid for copper drawing has a short service life, generally less than one year. The loss of the wire drawing die is relatively serious, so the requirements for the wire drawing die are relatively high, and the heat release...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C10M173/02C10N40/24C10N30/06C10N30/10C10N30/04
CPCC10M173/02C10N2030/04C10N2030/06C10N2030/10C10N2040/24C10N2040/244
Inventor 李小琴徐庭元陈明陈超黄超邓海军毛黎明
Owner JIANGSU ZHONGMEI CABLE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap