A method for producing electrolytic nickel

An electrowinning and electrowinning cell technology, applied in the field of metallurgy, can solve the problems affecting the optimization of technical and economic indicators, low content, etc., and achieve the effects of improving chemical quality and physical appearance quality, optimizing process, and reducing chemical composition.

Active Publication Date: 2017-12-01
JINCHUAN GROUP LIMITED
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the catholyte of nickel electrolysis, in addition to containing H + In addition, it often contains a small amount of metal ions such as copper, iron, cobalt, zinc and other harmful impurities. Although the content of these impurity ions is very low, the standard electrode potential is higher than that of Ni 2+ Positive Cu 2+ , Pb 2+ Plasma is prior to the reduction and precipitation of nickel ions, so the anolyte produced by electrowinning can be purified to a certain extent after electrolysis; this process has the following defects: (1) The impurity content of the chemical composition of the anolyte is lower than that of the catholyte, so return to the previous process according to the design process—leaching The batching process is carried out, and the solution produced after leaching is purified and used as catholyte; (2) the anolyte is returned to the previous process for batching, containing 20-25g / L of acid, and a certain amount of industrial sulfuric acid needs to be added during the liquid preparation, which affects the technical and economic indicators. Optimized, the unit consumption of industrial sulfuric acid reaches more than 700Kg / t·Ni

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for producing electrolytic nickel
  • A method for producing electrolytic nickel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] A method for electrolytic nickel deposition of the present invention will be further described in detail below in conjunction with the accompanying drawings.

[0021] Such as figure 1 , figure 2 As shown, the purpose of the present invention is to provide a Ni9996 electrolytic nickel production method, the anolyte generated in the electrolytic process is diffused and dialysis to make the pH reach 2.5-3.5, and enter the electrolytic cell as the electrolytic catholyte to produce high-quality electrolytic deposition. nickel. The cathode of the electrowinning cell is not covered with a diaphragm bag, and the anode is a titanium-based iridium-coated anode. After diffusion dialysis, the anolyte recovers a sulfuric acid concentration of 16-28g / L and returns to the front-end leaching process for batching. After industrial application, the chemical quality and physical appearance quality of electrodeposited nickel are improved, the process is optimized, and the production an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a method for producing electrodeposited nickel. Anode liquor generated in the electrodeposition process is used as a raw material. The content of Ni2+ is larger than or equal to 75 g / L, the content of Cu2+ is smaller than 0.001 g / L, the content of Fe2+ is smaller than 0.001 g / L, the content of Co2+ is smaller than 0.001 g / L, the content of Pb2+ is smaller than 0.0002 g / L, and the content of Zn2+ is smaller than 0.0002 g / L. The pH of the anode liquor is made to reach 2.5-3.5 after diffusion and dialysis of special negative ions, so that the anode liquor serving as electrodeposition catholyte enters an electrodeposition tank to produce the high-quality electrodeposited nickel; due to the fact that small granules which are not completely filtered, residual oil and organisms in the electrodeposition catholyte are adsorbed onto a plate surface, purification of the catholyte is achieved to a certain extent, and after acid modulation, a solution meets the production requirement of the electrodeposited Ni9996.

Description

technical field [0001] The invention relates to the field of metallurgy, in particular to a method for producing electrolytic nickel. Background technique [0002] At present, the electrolytic nickel manufacturers in the world all use the leaching-insoluble anode diaphragm electrolysis production process in the electrolytic nickel production. The anolyte produced in the electrolytic deposition process is returned to the leaching process as an acidic solution for batching. The anode of the electrowinning process adopts an insoluble anode, so that the metal to be extracted in the electrolyte is deposited and precipitated on the cathode, so as to achieve the purpose of extracting the metal. In the catholyte of nickel electrolysis, in addition to containing H + In addition, it often contains a small amount of metal ions with harmful impurities such as copper, iron, cobalt, and zinc. Although the content of these impurity ions is very low, the standard electrode potential is hig...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C25C1/08
CPCC25C1/08
Inventor 李瑞基雷军鹏陈涛卫媛闫刚刚徐军章梁照敏
Owner JINCHUAN GROUP LIMITED
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products