A kind of water-based antirust paint and preparation method thereof

A water-based anti-rust paint, water-based paint technology, applied in anti-corrosion coatings, polyester coatings, coatings, etc., can solve problems such as complex construction processes, and achieve good thermal stability, good anti-rust function, and safe use

Active Publication Date: 2016-10-19
LIAOYANG YIBANG NEW BUILDING MATERIALS GRP CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the above-mentioned water-based metal antirust paint adopts the mode of separate construction of primer and top coat, and the construction process is complicated.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of water-based antirust paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0018] A water-based antirust paint of the present invention, taking blue as an example, it includes the following raw materials in parts by mass: 650 parts of acrylic modified alkyd resin emulsion, 113 parts of deionized water, 100 parts of pigment and filler, 9 parts of rheological agent 1 part, 4 parts of dispersant, 2 parts of wetting agent, 3 parts of defoamer, 1 part of bactericide, 80 parts of film-forming aid, 20 parts of co-solvent, 5 parts of flash rust agent, 6 parts of multi-functional additive, thickener 6 parts of drug solution.

[0019] The above-mentioned pigments and fillers include 20 parts of R501 titanium dioxide, 10 parts of phthalocyanine blue pigment, 20 parts of precipitated barium sulfate, and 50 parts of aluminum tripolyphosphate;

example 2

[0021] A water-based antirust paint of the present invention, taking yellow as an example, it includes the following raw materials in parts by mass: 650 parts of acrylic modified alkyd resin emulsion, 115 parts of deionized water, 100 parts of pigment and filler, and 9 parts of rheological agent , 4 parts of dispersant, 2 parts of wetting agent, 3 parts of defoamer, 1 part of bactericide, 80 parts of film-forming aid, 20 parts of co-solvent, 5 parts of flash rust agent, 6 parts of multi-functional additive, thickener 4 parts of the solution.

[0022] The above-mentioned pigments and fillers include 20 parts of R501 titanium dioxide, 60 parts of medium chrome yellow powder, and 20 parts of aluminum tripolyphosphate;

example 3

[0024] A water-based antirust paint of the present invention, taking gray as an example, it includes the following raw materials in parts by mass: 650 parts of acrylic modified alkyd resin emulsion, 115 parts of deionized water, 100 parts of pigment and filler, and 9 parts of rheological agent , 4 parts of dispersant, 2 parts of wetting agent, 3 parts of defoamer, 1 part of bactericide, 80 parts of film-forming aid, 20 parts of co-solvent, 5 parts of flash rust agent, 6 parts of multi-functional additive, thickener 8 parts of the solution.

[0025] The above-mentioned pigments and fillers include 25 parts of R501 titanium dioxide, 15 parts of iron black powder, 20 parts of aluminum tripolyphosphate, and 40 parts of precipitated barium sulfate;

[0026] Preferably, the mass-number ratio of thickener to water in the thickener solution is 1:1.

[0027] The preparation process steps of water-based antirust paint are as follows:

[0028] (1) First, add rheological agent, FA365 di...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

An aqueous anti-rusting paint and a preparation method therefor. The paint is characterized in that: the raw materials in a formula in parts by mass are as follow: 600-700 parts of an acrylate modified alkyd resin emulsion, 100-120 parts of deionized water, 90-110 parts of pigments and fillers, 5-10 parts of a rheological agent, 5-10 parts of a dispersant, 1-5 parts of a defoamer, 1-3 parts of a bactericide, 70-90 parts of film forming auxiliaries, 15-25 parts of a co-solvent, 3-8 parts of a flash-rust agent, 5-10 parts of a multi-functional agent and 4-10 parts of a thickener solution. The process steps comprises: dispersing, milling, paint mixing, thickening, filtering and packaging. According to the present invention, water is used as a dispersion medium, multiple anti-rusting mechanism of physical, chemical and the like are used to prepare and produce the anti-rusting industrial paint. The paint combines an undercoat and a finishing coat and is constructed at one-time, so that the mode that the undercoat and the finishing coat of the conventional paint are constructed separately is broken. The paint is unequalled in environmental protection performance, good in salt-spray resistance and weather resistance and strong in anti-rusting function, and is an excellent product of a new generation that can replace the traditional anti-rusting paint. The paint has water solubility and non-flammable property, and is safe in use, and the paint is good in water resistance and good in thermal stability, and has a good anti-rusting function even in a high-temperature state.

Description

technical field [0001] The invention belongs to the technical field of paint manufacture, and in particular relates to a water-based antirust paint with an acrylic modified alkyd resin emulsion as a base material and a preparation method thereof. Background technique [0002] The antirust paint currently used is roughly two types: oily and water-based. Oil-based antirust paint makes it difficult to remove the greasy surface of the material, so it is rarely used. Oil-based antirust paint is easy to use and low in price, but because it contains toxic substances such as nitrite and chromate, it is harmful to operators. Rust requirements. [0003] The water-based metal anti-rust paint is made of metal strong chelating agent phytate as the main component, and is compounded with several other water-based additives. Phytate is a natural non-toxic organic chemical product extracted from food crops. When it is used as an antirust agent for magnetic materials, it can quickly chelat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D167/08C09D5/08
Inventor 崔桐嘉孙宝财
Owner LIAOYANG YIBANG NEW BUILDING MATERIALS GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com