Clay-base sand stabilizing material with water-saving temperature-regulating sand stabilizing function

A functional clay technology, applied in the field of clay-based sand-fixing materials, can solve the problems of reducing material degradation ability, secondary hazards, and increasing material costs, and achieve the effects of easy promotion and application, avoiding reprocessing, and low cost

Active Publication Date: 2015-08-19
NORTHWEST NORMAL UNIVERSITY
View PDF10 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantage of this invention is that a large amount of water glass and organic polymer materials are used in the raw materials, and such sand-fixing agents will still cause secondary harm to the environment
Chinese patent (CN 103289017 A) uses clay as the main raw material to graft and copolymerize acrylamide and bio-glue to obtain sand-fixing agent. Although the invention mentions the effect of water retention and heat preservation, the use of polyacrylamide in large quantities increases the cost of materials and reduces The degradation ability of the material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Clay-base sand stabilizing material with water-saving temperature-regulating sand stabilizing function
  • Clay-base sand stabilizing material with water-saving temperature-regulating sand stabilizing function
  • Clay-base sand stabilizing material with water-saving temperature-regulating sand stabilizing function

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] Raw material ratio: by weight

[0051] 60 parts of clay, 15 parts of biomass waste, 5 parts of animal bones, 5 parts of animal manure, 2 parts of perlite, 3 parts of lactic acid, 3 parts of potassium hydroxide, 1 part of phosphoric acid, 1 part of lecithin, 5 parts of methyl cellulose share;

[0052] Preparation Process:

[0053] Mix the pulverized biomass waste and animal manure and place them in a reaction kettle, add tap water to make a suspension with a mass fraction of 75%; add potassium hydroxide, activate at 100°C for 15 hours, and then add phosphoric acid to proceed and, obtaining a mixed suspension of activated biomass waste and animal manure;

[0054] Crush animal bones, pass through a 400-mesh sieve, add water to make a 10% suspension, put it in a reaction kettle, and activate it at 100°C for 2 hours to obtain an activated animal bone suspension;

[0055] Mix activated biomass waste with animal manure suspension, activated animal bone suspension, clay, per...

Embodiment 2

[0057] Raw material ratio: by weight

[0058] 60 parts of clay, 10 parts of biomass waste, 5 parts of animal bones, 5 parts of animal manure, 2 parts of perlite, 3 parts of lactic acid, 3 parts of potassium hydroxide, 1 part of phosphoric acid, 1 part of lanolin, hydroxypropyl methyl 5 parts of cellulose;

[0059] Preparation Process:

[0060] Mix the pulverized biomass waste and animal manure and place them in a reaction kettle, add tap water to make a suspension with a mass fraction of 65%; add potassium hydroxide, activate at 95°C for 15 hours, and then add phosphoric acid to proceed and, obtaining a mixed suspension of activated biomass waste and animal manure;

[0061] Crush animal bones, pass through a 400-mesh sieve, add water to make a 5% suspension, put it in a reaction kettle, and activate it at 55°C for 5 hours to obtain an activated animal bone suspension;

[0062] Mix the activated biomass waste with animal manure suspension, activated animal bone suspension, c...

Embodiment 3

[0064] Raw material ratio: by weight

[0065] 85 parts of clay, 8 parts of biomass waste, 2 parts of animal bone, 1 part of animal manure, 1 part of perlite, 1 part of lactic acid, 0.3 part of potassium hydroxide, 0.1 part of phosphoric acid, 0.6 part of lanolin, 1 part of hydroxyethyl cellulose share;

[0066] Preparation Process:

[0067] Mix the pulverized biomass waste and animal manure and place them in a reaction kettle, add tap water to make a suspension with a mass fraction of 55%; add potassium hydroxide, activate at 85°C for 15 hours, and then add phosphoric acid to proceed and, obtaining a mixed suspension of activated biomass waste and animal manure;

[0068] Crush animal bones, pass through a 400-mesh sieve, add water to make an 8% suspension, put it in a reaction kettle, and activate it at 65°C for 5 hours to obtain an activated animal bone suspension;

[0069] Mix activated biomass waste with animal feces suspension, activated animal bone suspension, clay, pe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a multifunctional clay-base sand stabilizing material integrating a water saving function, a temperature regulation function and a sand stabilizing function, and belongs to the field of sand control and sand stabilization. The sand stabilizing material adopts clay, biomass waste, animal bones, animal excrement, perlite, lactic acid, potassium hydroxide, phosphoric acid, natural emulsifier and cellulose as raw materials and is prepared in a given process. When in use, the clay-base sand stabilizing material is directly sprayed onto the surface of desert by utilizing a spraying device, and the crust thickness is controlled at 5mm to 10mm. The experiment shows that the product integrates the temperature regulation function, the water saving function and the sand stabilizing function; moreover, raw materials are natural products, so that the cost is low, the preparation process is simple, secondary environmental pollution is avoided, and the clay-base sand stabilizing material plays a positive role in restoring and rebuilding vegetation of a desert area.

Description

technical field [0001] The invention relates to a clay-based sand-fixing material, in particular to a clay-based sand-fixing material with water-saving, temperature-regulating and sand-fixing functions, belonging to the field of sand control and sand fixing. Background technique [0002] Land desertification is a worldwide ecological environment problem. According to the statistics of the United Nations Environment Program (UNEP), the areas that have been and are expected to be affected by desertification account for 35% of the global land area. my country is one of the countries with severe desertification in the world. The results of the national survey of deserts, Gobi and sandy land and desertification investigations show that the desertification land area in my country is 2.622 million square kilometers, accounting for 27.4% of the country's land area. Nearly 400 million people are affected by desertification. 120 billion yuan, ecology, society and economy have been se...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09K17/40C05G3/04C09K105/00C05G3/80
CPCC05G3/80C09K17/40C09K2105/00
Inventor 雷自强周鹏鑫张哲马国富马德龙
Owner NORTHWEST NORMAL UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com