A kind of manufacturing method of glazed tile and its product

A manufacturing method and technology of polished glazed tiles, which are applied in the field of ceramic tiles, can solve problems such as surface waves of polished glazed tiles, achieve the effect of solving pinhole concave glaze on the glazed surface, solving the stability problem of the production process, and ensuring smoothness

Active Publication Date: 2017-11-10
FOSHAN DONGPENG CERAMIC +2
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to propose a manufacturing method of glazed tiles, which can solve the problem of the corrugated surface of glazed tiles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of manufacturing method of glazed tile and its product

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Such as figure 1 As shown, a glazed glazed tile of this embodiment includes a base layer 1, a printing layer 2, a protective glaze layer 3 and a transparent glaze layer 4 from bottom to top, wherein the thickness of the base layer 1 is 8.5mm, and the printing layer The thickness of the layer is 0.05mm, the thickness of the protective glaze layer is 0.2mm, and the thickness of the transparent glaze layer is 0.8mm.

[0025] The above-mentioned manufacturing method of polished glazed tiles with a specification of 1000*1000mm, the steps include in sequence:

[0026] A. Press the ceramic powder to form adobe, control the temperature of the adobe at 65°C after drying, and apply 380g of bottom glaze on the adobe to form the bottom adobe layer 1;

[0027] B. On the bottom base layer 1 after the step A, pass screen printing and dry to form a printing layer 2, control the temperature of the brick body at 55°C, apply protective glaze 350g to form a protective glaze layer 3, and t...

Embodiment 2

[0033] Such as figure 1 As shown, a kind of polished glazed tile of the present embodiment comprises a bottom base layer 1, a printing layer 2, a protective glaze layer 3 and a transparent glaze layer 4 from bottom to top, wherein the thickness of the bottom base layer 1 is 6mm, and the printing layer The thickness is 0.08mm, the thickness of the protective glaze layer is 0.1mm, and the thickness of the transparent glaze layer is 1.0mm.

[0034] The above-mentioned manufacturing method of polished glazed tiles with a specification of 1000*1000mm, the steps include in sequence:

[0035] A. Spray and granulate the raw material ingredients by ball milling and then press to form adobe. After drying, control the temperature of the adobe at 75°C and apply 300g of bottom glaze on the adobe to form the bottom adobe layer 1;

[0036] B. On the bottom base layer 1 after the step A, the printing layer 2 is formed by inkjet printing and drying, the temperature of the brick body is contro...

Embodiment 3

[0042] Such as figure 1 As shown, a kind of polished glazed tile of the present embodiment comprises a bottom base layer 1, a printing layer 2, a protective glaze layer 3 and a transparent glaze layer 4 from bottom to top, wherein the thickness of the base base layer 1 is 9mm, and the printing layer The thickness is 0.06mm, the thickness of the protective glaze layer is 0.15mm, and the thickness of the transparent glaze layer is 0.9mm.

[0043] The above-mentioned manufacturing method of polished glazed tiles with a specification of 1000*1000mm, the steps include in sequence:

[0044] A. Spray and granulate the raw materials by ball milling and then press to form adobe. After drying, control the temperature of the adobe at 70°C and apply 400g of bottom glaze on the adobe to form the bottom adobe layer 1;

[0045]B. On the bottom base layer 1 after the step A, the printing layer 2 is formed after roller printing and drying, the temperature of the brick body is controlled at 55...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a glazed brick manufacturing method and product, the method comprises the following steps: A, proportioning raw materials for ball milling for spray granulation to press into a brick blank, after drying, applying ground coat to the brick blank; B, printing the brick blank treated by the step A, drying, and applying protective glaze; C, bisque firing; D, applying a layer of transparent glaze to the brick blank treated by the step C, and then drying; and E, putting the brick blank treated by the step D into a kiln for firing, then using a non elastic module for grinding, packaging and storing. The burned product can be ground by use of the non elastic module for the reason that the protective glaze layer and the transparent glaze layer in a printing layer are thick and smooth, and the surface ultra smooth and mirror effect can be ensured.

Description

technical field [0001] The invention relates to the field of manufacturing ceramic tiles, in particular to a method for manufacturing glazed tiles and products thereof. Background technique [0002] Polished glazed tiles, also known as fully polished glazed tiles, are a new architectural ceramic product in recent years. It combines the advantages of polished tiles, antique tiles, and porcelain tiles. It solves the defect that semi-polished bricks are easy to hide dirt. It has the glossiness and porcelain hardness of polished bricks. It also has the high imitation effect of the glazed surface of antique bricks and the rich printing effect of glazed tiles. The existing polished glazed brick is formed by printing a decorative layer on the brick body, applying a 0.5-1.5 mm transparent glaze layer on the decorative layer, firing, and polishing with an elastic module. Due to the thin transparent glaze layer and the use of elastic modules, the contact between the glaze layer and t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/89C04B41/86
Inventor 王华明
Owner FOSHAN DONGPENG CERAMIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com