One-step-feeding method for preparing phthalic-anhydride-modified epoxy acrylate, and formula thereof

A technology of epoxy acrylate and phthalic anhydride, which is applied in the field of preparing phthalic anhydride-modified epoxy acrylate by one-step feeding method, which can solve the problems of long-term contact with human body, pollution of the working environment, and difficult feeding methods, so as to improve the working environment and optimize the process flow , to solve the effect of acid value difficult to drop

Inactive Publication Date: 2013-07-24
ZHONGSHAN KETIAN ELECTRONICS MATERIALS
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The defect of this preparation method: after the first step reaction finishes, need to cool down and just can drop into epoxy resin 128, because the reaction speed of epoxy resin and intermediate is very fast under high temperature; The feeding method adopted by a large-scale factory is difficult to operate; if the manhole is opened and epoxy resin 128 is poured through the manhole, the materials in the reactor will be emitted under high temperature conditions, causing serious pollution to the working environment on site, and long-term contact may even cause serious harm to the human body

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • One-step-feeding method for preparing phthalic-anhydride-modified epoxy acrylate, and formula thereof
  • One-step-feeding method for preparing phthalic-anhydride-modified epoxy acrylate, and formula thereof
  • One-step-feeding method for preparing phthalic-anhydride-modified epoxy acrylate, and formula thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0029] In the preferred embodiment of the present invention, a kind of preparation method and formula for preparing phthalic anhydride modified epoxy acrylate are provided, and its preparation method comprises the following steps:

[0030] Step 1) Feeding, choose 32.45% epoxy resin 128 by weight percentage, 24.68% phthalic anhydride, 22.47% reactive diluent tripropylene glycol diacrylate, 20.05% hydroxyethyl acrylate, 0.204% catalyst triethylene Amine, 0.063% inhibitor p-hydroxyanisole, 0.083% antioxidant 2,6-di-tert-butyl-4-methylphenol; all raw materials except reactive diluent tripropylene glycol diacrylate Put it into the reactor at one time, seal all the valves and vacuumize the reactor after feeding, so that the inside of the reactor is in a vacuum state, and then close the vacuum valve;

[0031] Step 2) Stop vacuuming, quickly feed nitrogen, make the reactor full of nitrogen, until the reactor is in a state of normal pressure, adjust the nitrogen flow to 50-70L / hr, open...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a one-step-feeding method for preparing phthalic-anhydride-modified epoxy acrylate, and a formula thereof. The finished product is prepared from the components of, by weight, 32.4% of epoxy resin 128, 24.7% of phthalic anhydride, 22.45% of a reactive diluent, 20.1% of hydroxyethyl acrylate, 0.21% of a catalyst, 0.06% of a polymerization inhibitor, and 0.08% of an anti-oxidant, wherein an optional variable range of the amounts of epoxy resin 128, reactive diluent, phthalic anhydride, and hydroxyethyl acrylate is respectively 0.15%, and an optional variable range of the amounts of the catalyst, the polymerization inhibitor, and the anti-oxidant is respectively 0.005%. A synthesizing method is the one-step feeding method. During the entire reaction process, through the optimal control and adjustment upon process parameters such as acid value, temperature, nitrogen flow and reaction time, the phthalic-anhydride-modified epoxy acrylate finished product with stable application performance, stable storage performance, moderate viscosity, and water-white transparent color is obtained.

Description

technical field [0001] The invention relates to chemical products and a preparation method thereof, in particular to a method for preparing phthalic anhydride-modified epoxy acrylate by a one-step feeding method and a formula thereof. Background technique [0002] The existing process adopts a step-by-step feeding method: put in hydroxyethyl acrylate and phthalic anhydride and heat them to react at 110°C, judge which stage the reaction has progressed according to the detected acid value; after the first step of reaction is in place, cool the materials to 90 ℃, and then put in epoxy resin 128 for temperature rise reaction until the acid value drops to 2.0-2.5mgKOH / g. The defect of this preparation method: after the first step reaction finishes, need to cool down and just can drop into epoxy resin 128, because the reaction speed of epoxy resin and intermediate is very fast under high temperature; The feeding method adopted by a large-scale factory is difficult to operate; if ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08G59/16C08G59/42C08K5/13C08F283/10
Inventor 龙伟新陈志红
Owner ZHONGSHAN KETIAN ELECTRONICS MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products