Preparation method of reconstituted tobacco with aroma characteristic strengthening effect

A technology for remanufacturing tobacco leaves and aroma, which is applied in the direction of preparing tobacco, tobacco, and treating tobacco to achieve industrialized production, good development and application prospects, and reduce manufacturing costs

Inactive Publication Date: 2013-06-12
HONGYUN HONGHE TOBACCO (GRP) CO LTD
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Although there have been reports on the preparation of functional reconstituted tobacco leaves from non-tobacco plants as raw materials, there have been no reports on the preparation of reconstituted tobacco leaves from the residue left after the conventional extraction and utilization of traditional Tibetan medicinal plants

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of reconstituted tobacco with aroma characteristic strengthening effect

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Example 1——Preparation and application of reconstituted tobacco leaves with enhanced aroma characteristics 1

[0023] 1. Preparation of reconstituted tobacco leaves

[0024] (1) Extract 100 g of Tibetan woody incense, 600 g of tobacco stems and 300 g of tobacco fragments with water at 60°C for 90 min, and separate the water extract and insoluble matter;

[0025] (2) Beat the insoluble matter, apply papermaking technology and equipment, and make a substrate;

[0026] (3) Vacuum concentrate the water extract to a density of 1-1.2 g / cm 3 , and backcoat the concentrated solution on the formed substrate to obtain the required reconstituted tobacco leaves.

[0027] 2. Addition experiments in cigarettes

[0028] The prepared shredded reconstituted tobacco leaves were applied to the Yunyan (impression) leaf group formula at a ratio of 6%, and the leaf group mixed with reconstituted tobacco leaves without Tibetan woody fragrance was used as the control group.

[0029] 3. Smo...

Embodiment 2

[0033] Example 2——Preparation and application of reconstituted tobacco leaves with enhanced aroma characteristics 2

[0034] 1. Preparation of reconstituted tobacco leaves

[0035] (1) Extract 100 g of Tibetan woody incense, 500 g of tobacco stems and 400 g of tobacco fragments with water at 70°C for 60 min, and separate the water extract and insoluble matter;

[0036] (2) Beat the insoluble matter, apply papermaking technology and equipment, and make a substrate;

[0037] (3) Vacuum concentrate the water extract to a density of 1-1.2 g / cm 3 , and backcoat the concentrated solution on the formed substrate to obtain the required reconstituted tobacco leaves.

[0038] 2. Addition experiments in cigarettes

[0039] The prepared shredded reconstituted tobacco leaves were applied to the Yunyan (impression) leaf group formula at a ratio of 6%, and the leaf group mixed with reconstituted tobacco leaves without Tibetan woody fragrance was used as the control group.

[0040] 3. Smo...

Embodiment 3

[0044] Example 3——Preparation and application of reconstituted tobacco leaves with enhanced aroma characteristics 3

[0045] 1. Preparation of reconstituted tobacco leaves

[0046] (1) Extract 200 g of Tibetan woody incense, 500 g of tobacco stems and 300 g of tobacco fragments with water at 90°C for 30 min, and separate the water extract and insoluble matter;

[0047] (2) Beat the insoluble matter, apply papermaking technology and equipment, and make a substrate;

[0048] (3) Vacuum concentrate the water extract to a density of 1-1.2 g / cm 3 , and backcoat the concentrated solution on the formed substrate to obtain the required reconstituted tobacco leaves.

[0049] 2. Addition experiments in cigarettes

[0050] The prepared shredded reconstituted tobacco leaves were applied to the Yunyan (impression) leaf group formula at a ratio of 6%, and the leaf group mixed with reconstituted tobacco leaves without Tibetan woody fragrance was used as the control group.

[0051] 3. Smo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of reconstituted tobacco with an aroma characteristic strengthening effect. The residue obtained after inula racemosa hook. f. for the traditional Tibetan medicines is subjected to the conventional extraction method is used as a raw material, is mixed with tobacco stems and chopped tobacco flakes in a proportion, is soaked with hot water and is extracted; the obtained insoluble is made into a substrate by a papermaking method; and the obtained water extract is used for coating the substrate to manufacture the reconstituted tobacco after being subjected to vacuum concentration treatment. The reconstituted tobacco is applied to a cigarette formula and has effects of enhancing woody aroma, faint scent and sweet aroma, strengthening the aroma characteristic and meanwhile reducing the stimulus and increasing the moisturizing feel. According to the method, the utilization rate of resource plant is increased, and the reduction in the manufacturing cost is facilitated.

Description

technical field [0001] The invention belongs to the technical field of reconstituted tobacco leaves, and in particular relates to a preparation method of reconstituted tobacco leaves capable of enhancing aroma characteristics. Background technique [0002] In today's cigarette industry, reconstituted tobacco has increasingly become an indispensable raw material in the cigarette industry. It plays a very important role in improving the internal quality of tobacco products, reducing tar content, changing smoke components, saving tobacco consumption, and stabilizing cigarette formula. role. [0003] With the continuous development of reconstituted tobacco technology, the application of non-tobacco plant materials in reconstituted tobacco has also been reported. Yao Ermin et al. used tea as an additive, added reconstituted tobacco leaves with different proportions of tea leaves to the leaf group to make cigarette samples, and the results showed that compared with the control sa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A24B3/14A24B15/24A24B3/12
Inventor 杨莹陈微胡巍耀高锐李俊谷凌军
Owner HONGYUN HONGHE TOBACCO (GRP) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com