A method of manufacturing a ferromagnetic core containing cao
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A manufacturing method and ferromagnetic core technology, applied in the direction of inductance/transformer/magnet manufacturing, inorganic material magnetism, electrical components, etc., can solve the problems of low mechanical strength of materials, unsuitable cutting, low saturation magnetic induction intensity, etc., and achieve small deformation, The effect of low porosity and slight deformation
Active Publication Date: 2016-05-04
TIANCHANG CITY ZHAOTIAN MAGNETOELECTRICITY TECH
View PDF4 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
The saturation magnetic induction of sendust core is generally about 5000-9000 Gauss, and the iron loss is relatively low, but the mechanical strength of its material is too low; the saturation magnetic induction of ferrite is about 2700-4200 Gauss, and the iron loss is quite good , but the saturation magnetic induction is too low, and it is not suitable for cutting
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0018] Embodiment 1: the manufacture method of the ferromagnetic core containing CaO, comprises the following steps:
[0019] (1) The ratio of raw materials is calculated in parts by weight (catties), reduced iron powder 74, iron oxide powder 14, MnO3.5, ZnO3.5, modified nano-carbon 2, boron oxide 2.4, CaO2.6, SnO 2 3.3, V 2 o 5 4. Fe 3 o 4 3.5, the modified nano-carbon is prepared by the following method:
[0020] a. After soaking the tree ashes with 12% sodium hydroxide solution for 2-3 hours;
[0021] b. Soak in 12% hydrochloric acid solution for 2-3 hours;
[0022] c. Wash with deionized water several times until the tree ash is neutral, then dry;
[0023] d. Grinding to 0.8-1.0 μm powder to obtain modified tree ash;
[0024] E, add the above-mentioned modified tree ash that is equivalent to its weight 4%, the nano silicon dioxide of 2.5% in nano-carbon, fully mix and obtain;
[0025] (2) Pre-calcination: Add water and dispersant to the raw materials except modifie...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
saturation magnetic induction
aaaaa
aaaaa
saturation magnetic induction
aaaaa
aaaaa
saturation magnetic induction
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses a CaO-containing ferromagnetic core manufacturing method, which comprises the following steps of: proportioning 72-75 parts of reduced iron powder by weight, 13-15 parts of oxidized iron powder by weight, 2.5-4.5 parts of MnO by weight, 3-4 parts of ZnO by weight, 1.5-2.5 parts of modified nano carbon by weight, 1.8-2.8 parts of boric oxide by weight, 2.3-2.8 parts of CaO by weight, 2.5-4 parts of SnO2 by weight, 3.7-4.3 parts of V2O5 by weight and 3.3-3.8 parts of Fe3O4 by weight, and then sequentially conducting pre-sintering, primary ball milling, secondary ball milling, molding and sintering to obtain a CaO-containing ferromagnetic core. The CaO-containing ferromagnetic core manufacturing method has the advantages that the magnetic core formula is reasonable, the preparation method is simple, the saturation induction density of the manufactured magnetic core is higher, the loss is lower, the temperature resistance is higher, the added modified nano carbon and the boric oxide can take a bridge bonding effect among different raw materials, the distribution of the used raw materials is better, the density is high, the crystal boundary resistivity is high, the porosity is low, the grains are large and uniform, the cracks are prevented from occurring during sintering, the texture is compact, the deformation is small, the raw material formula is reasonably improved, the deformation degree is small during sintering, and the magnetic core can be wire-cut, cut, ground and the like.
Description
technical field [0001] The invention belongs to powder metallurgy technology, in particular to a method for manufacturing a ferromagnetic core containing CaO. Background technique [0002] The saturation magnetic induction of the iron powder magnetic core is generally about 9000-11000 Gauss, and the iron loss is very large in the alternating electric field of 100-2000 Hz. The saturation magnetic induction of sendust core is generally about 5000-9000 Gauss, and the iron loss is relatively low, but the mechanical strength of its material is too low; the saturation magnetic induction of ferrite is about 2700-4200 Gauss, and the iron loss is quite good , but the saturation magnetic induction is too low, and it is not suitable for cutting. Contents of the invention [0003] In order to alleviate the deficiencies and defects of the prior art, the object of the present invention is to provide a method for manufacturing a ferromagnetic core containing CaO. [0004] In order to a...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01F1/09H01F41/02B22F3/16
Inventor 徐杰杨从会黄国祥刘京州曾性儒张忠仁王玉志
Owner TIANCHANG CITY ZHAOTIAN MAGNETOELECTRICITY TECH