Metal substrate with thermally-sprayed anti-sticking wear-resistant coating and preparation method as well as application thereof

A technology of metal substrates and wear-resistant coatings, which is applied in the direction of metal layered products, chemical instruments and methods, and layered products, can solve the problems of non-stick performance failure, large peeling force, and insufficient wear resistance, and achieve Light adhesive peel force, improved surface strength, excellent wear and scratch resistance

Active Publication Date: 2013-12-18
德清创智科技股份有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve and replace the non-stick coating "Teflon" traditionally used in various industrial fields, the peeling force of the hot melt adhesive is too large and the wear resistance is not enough to cause the short-term failure of the non-stick performance; The first object is a metal substrate with thermal spraying anti-sticking wear-resistant coating; the second object of the present invention is the preparation method of the above-mentioned metal substrate; the third object of the present invention is to provide Substrate drive roller

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Metal substrate with thermally-sprayed anti-sticking wear-resistant coating and preparation method as well as application thereof
  • Metal substrate with thermally-sprayed anti-sticking wear-resistant coating and preparation method as well as application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] like figure 1 Shown is a metal substrate 3 with thermal spraying anti-sticking and wear-resistant coating, the surface of the metal substrate 3 is provided with a nickel-based alloy coating 2, and the surface of the nickel-based alloy coating 2 is dispersed and bonded with silicon polymerization The material resin layer 1, the silicon polymer resin layer 1 is cured and cross-linked by addition type siloxane resin. The layer thickness of the nickel-based alloy coating 2 is 120 μm, and the surface hardness is HRC50˜HRC60.

[0029] The formulation of the nickel-based alloy coating 2 in this embodiment is as follows: C 0.5-1.1%, Si 3.0-5.5%, B 3.0-4.5%, Cr 15-30%, Fe=5.0%, and the balance is Ni.

[0030] The silicone polymer resin is commercially available from Ningbo Chemical Industry Co., Ltd.: A component: addition type siloxane; B component: composite platinum catalyst.

[0031] The above-mentioned method for the metal substrate with thermal spraying anti-sticking and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to anti-sticking wear-resistant treatment of a metal substrate, in particular to a metal substrate with a thermally-sprayed anti-sticking wear-resistant coating and a preparation method thereof as well as a driving roller adopting the substrate. A nickel-based alloy coating is arranged on the surface of the metal substrate with the thermally-sprayed anti-sticking wear-resistant coating, and a silicon polymer resin layer is arranged on the surface of the nickel-based alloy coating in a disperse combination mode. The invention also discloses a method for preparing the metal substrate with the thermally-sprayed anti-sticking wear-resistant coating as well as a driving roller adopting the metal substrate. The product disclosed by the invention has the advantages that the anti-sticking effect is improved, the service life is prolonged, the equipment maintenance and repair strength and period are reduced, the equipment service efficiency is increased, the product quality is improved, and the production cost is lowered.

Description

technical field [0001] The invention relates to the anti-adhesive and wear-resistant treatment of metal base materials, in particular to a metal base material with a heat-sprayed anti-stick and wear-resistant coating, a preparation method thereof and a driving roller using the base material. Background technique [0002] Applied to coating machines, printing machines, printing and dyeing machines, tape production machinery, diaper production machinery, etc. . The drive rollers of these machines often need to be in contact with the gluing surface, printing surface or printing and dyeing surface. The undried printing surface and printing and dyeing surface are easy to contaminate the roller and affect the surface pattern of the product. At present, "Teflon" is generally used to treat the surface of the roller. Such as Chinese utility model patent (application number: 200720199289.X application date: 2007-12-14) discloses a kind of anti-adhesive foil roller, used in automatic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B15/08B32B3/30
Inventor 沈健健陈峰张方权
Owner 德清创智科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com