Material for use in water-proofing and leakage-stopping grouting and preparation method thereof

A technology for waterproof plugging and waterproof coating, which can be used in building thermal insulation materials, chemical instruments and methods, and other chemical processes, etc., and can solve the problems of foam cracking, lack of flexibility, and poor waterproof durability of water-soluble polyurethane grouting materials. , to achieve stable performance and good durability

Inactive Publication Date: 2014-04-09
SHENZHEN AIDAKAI WATERPROOF ENG CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, since the expansion of this material is caused by the foaming of the water reaction, when the water content of the structural layer injected with the slurry is reduced or even after the space filled with foam is dried, this foamed gel-like consolidated body material will gradually form. A certain amount of shrinkage will cause subtle changes to the original good waterproof effect. After a certain period of time (about one year), some parts will often leak again.
Therefore, the water-soluble polyurethane grouting material does not have good waterproof durability for the waterproof plugging of the leaking part where the upstream surface is not long-term water-containing
Compared with water-soluble polyurethane grouting fluid, another grouting material used for waterproofing and plugging is oil-soluble polyurethane grouting fluid. Although this material generally does not shrink or re-expand due to changes in the surrounding environment after reaction foaming, it does This kind of material lacks flexibility after foaming, and the stress caused by the deformation of the surrounding structure of the foam is easy to tear the foam used for waterproofing, so that the leaking weak parts will leak again

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] The steps are as follows: (the main ingredient is based on 10 kg)

[0023] In the first step, put 10 kg of component A material (main material) in the mixing tank;

[0024] Step 2: Pour 0.8 kg of component B material (auxiliary 1) into the mixing tank and stir at a low speed of 150-200 rpm for 1-2 minutes;

[0025] Step 3: Pour 0.4 kg of C component material (auxiliary 2) into the mixing tank and stir at a medium speed of 200-300 rpm for 2-3 minutes.

[0026] The fourth step, the finished product is put into use.

[0027] illustrate:

[0028] 1) Above, component A is the main ingredient, B and C are additives;

[0029] 2) Prepare according to the above addition ratio, the initial setting time of the mixture is about 7-8 hours, and the final setting time is 13-15 hours.

[0030] 3) The compounding of the mixed materials must be carried out according to the required steps.

[0031] 4) The mixing tool can be a hand-held electric mixer, and it can also be mixed with a ...

Embodiment 2

[0035] The steps are as follows: (the main ingredient is based on 10 kg)

[0036] In the first step, put 10 kg of component A material (main material) in the mixing tank;

[0037] Step 2: Pour 1 kg of component B material (auxiliary 1) into the mixing tank and stir at a low speed of 150-200 rpm for 1-2 minutes;

[0038] Step 3: Pour 0.5 kg of C component material (auxiliary 2) into the mixing tank and stir at a medium speed of 200-300 rpm for 2-3 minutes.

[0039] The fourth step, the finished product is put into use.

[0040] illustrate:

[0041] 7) Above, component A is the main ingredient, B and C are additives;

[0042] 8) Prepare according to the above adding ratio, the initial setting time of the mixture is about 7-8 hours, and the final setting time is 13-15 hours.

[0043] 9) The compounding of the mixture must be carried out according to the required steps.

[0044] 10) The mixing tool can be a hand-held electric mixer, and it can also be mixed with a stick when ...

Embodiment 3

[0048] The steps are as follows: (the main ingredient is based on 10 kg)

[0049] In the first step, put 10 kg of component A material (main material) in the mixing tank;

[0050] Step 2: Pour 1.3 kg of B component material (auxiliary 1) into the mixing tank and stir at a low speed of 150-200 rpm for 1-2 minutes;

[0051] Step 3: Pour 0.65 kg of C component material (auxiliary 2) into the mixing tank and stir at a medium speed of 200-300 rpm for 2-3 minutes.

[0052] The fourth step, the finished product is put into use.

[0053] illustrate:

[0054] 1) Above, component A is the main ingredient, B and C are additives;

[0055] 2) Prepare according to the above adding ratio, the initial setting time of the mixture is about 4-5 hours, and the final setting time is 8-9 hours.

[0056] 3) The compounding of the mixed materials must be carried out according to the required steps.

[0057] 4) The mixing tool can be a hand-held electric mixer, and it can also be mixed with a stick...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a new material for water-proofing and leakage-stopping grouting, which belongs to the technical field of new materials and is particularly suitable to be used in grouting for stopping the leakage of leakage water in a structure of a concrete building. The new material for waterproof and leakage-stopping grouting of the invention is prepared by mixing a waterproof paint and an assistant, and is characterized in that: the waterproof paint is emulsified polymer building waterproof paint; and the assistant is prepared by mixing solvent-free polyurethane and polyurethane curing agent, wherein based on the total amount of 100 part of the emulsified polymer building waterproof paint, the solvent-free polyurethane is 8 to 20 parts and the polyurethane curing agent is 4 to 10 parts. Compared with the prior art, the new material has the advantages that: the mixed materials can gel through cure reaction within a certain time period to proof water and stop leakage; and the cured material has stable performance, high acid, alkali and aging resistance and high durability.

Description

technical field [0001] The invention relates to a grouting, waterproof and leak-stopping material belonging to the technical field of materials, and is a material particularly suitable for grouting and plugging leaking water in concrete building structures. technical background [0002] In the prior art, the leaking water of concrete building structures is used for grouting and plugging materials. In the invention patent publication number: CN1924534, a new waterproof plugging method is proposed in "Methods for Detection and Plugging of Water Leakage Sources in Concrete Buildings" Leakage method, that is: through the grouting hole, the water-soluble polyurethane plugging agent added with the grouting liquid hardening regulator is injected through the grouting hole, so that the grout passes through the roof to form a layer between the roof waterproof material and the roof slab. New connected waterproofing. Water-soluble polyurethane chemical grouting material is a polymer gr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09K3/12E04B1/66
Inventor 李海军
Owner SHENZHEN AIDAKAI WATERPROOF ENG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products