Titanium leaking method for reactor for titanium sponge production

A technology of reactor and titanium sponge, which is applied in the direction of metal material coating process, coating, solid-state diffusion coating, etc., can solve the problems of unstable iron impurity content, labor and time-consuming, and reduced service life, so as to avoid poor quality Stability, broad application prospects, and the effect of improving service life

Inactive Publication Date: 2012-05-30
SICHUAN HENGWEI TITANIUM TECH CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, this single method of titanium infiltration has the following defects: 1. The content of iron impurities in the sponge titanium product produced for the first time by the reactor after titanium infiltration is unstable, and the titanium infiltration process conditions are affected by various factors, and the titanium infiltration effect is sometimes good 2. It needs to consume a certain amount of high-quality and expensive titanium powder; 3. The process of infiltrating titanium requires a certain amount of energy, which is labor-intensive and time-consuming; 4. For the original limited number of uses For the reactor, its service life is reduced due to the high temperature heating operation during the titanium infiltration process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Titanium leaking method for reactor for titanium sponge production
  • Titanium leaking method for reactor for titanium sponge production

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0020] The reactor for sponge titanium production (maximum production capacity is 12t) is acid leached to remove rust, then washed and dried, and 300-1000kg of magnesium ingots are placed in the reactor, and the temperature is controlled to be 700-850°C, and then 1200-4000kg is added. Titanium tetrachloride is subjected to reduction reaction to infiltrate titanium. At the end of titanium infiltration, add magnesium ingots and liquid magnesium required for normal production of sponge titanium, add titanium tetrachloride required for normal production, and carry out normal reduction production of sponge titanium. 12 new reactors (numbered 10-21) were infiltrated with titanium respectively, and then the new reactors after infiltration of titanium were used to produce titanium sponge, and the impurity content of the produced titanium sponge was detected. The results are shown in Table 2.

[0021] The same type of reactor is subjected to titanium infiltration by ordinary methods fo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method of titanizing an reactor for titanium sponge production and belongs to the chemical industry field of smelting non-ferro metals. The invention provides a titanizing method for reducing impurity content of iron and the like in titanium sponge firstly produced by a novel reactor.The titanizing method of a novel reactor for titanium sponge production comprises the following steps: a, performing acid leaching to a novel reactor for derusting, and then rinshing and drying; b. adding suitable amount of magnesium and fine titanic chloride, increasing the temperatureto 700-850 DEG C to perform a reduction reaction, and then titanizing; wherein, the adding amount of magnesium and fine titanic chloride is determined on the basis that the titanium generated in the reduction reaction forms a titanizing layer on the wall of the novel reactor. The method reduces content of foreign matters such as iron in the titanium sponge firstly produced by a novel reactor, improves service life of the reactor, reduces the titanizing cost, provides a novel selection and breaks a new path to the titanizing technique of a novel reactor for producing titanium sponge, and has an expansive application prospect.

Description

technical field [0001] The invention relates to a titanium infiltration method of a reactor for producing sponge titanium, and belongs to the field of non-ferrous metal chemical smelting. Background technique [0002] Magnesium reduction vacuum distillation method to produce sponge titanium is to react raw magnesium and refined titanium tetrachloride in a reactor under certain conditions to form sponge titanium. The reactor used is usually made of heat-resistant boiler steel plate. Since the raw materials and products directly contact the reactor and other related steel components during the production process, such as: sieve plates, magnesium chloride tubes, etc., iron impurities may dissolve into the raw magnesium liquid or directly into the finished titanium sponge in the form of alloys, thereby affect product quality. [0003] In order to prevent a large amount of impurities in steel from being transferred into titanium sponge, since the 1970s, through the efforts of en...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C10/20C22B34/12C22B5/00
Inventor 巴升林董震宇
Owner SICHUAN HENGWEI TITANIUM TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products