High tensile strength hot dip plated steel sheet and method for production thereof
A high tensile strength, hot-dip coating technology, applied in hot-dip coating process, manufacturing tools, heat treatment furnace, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0130] Slabs having various compositions shown in Table 1 were heated to 1200°C and hot rolled at a finish rolling temperature of 850-900°C. Each hot-rolled steel strip was then pickled and cold-rolled at a reduction ratio of 77% to obtain a cold-rolled steel sheet with a thickness of 0.7 mm, which was recrystallized annealed with CAL and CGL under the conditions shown in Table 2- It is further processed in the steps of pickling-heating before electroplating-hot dipping. In addition, as a treatment atmosphere, (7 vol% H 2 +N 2 ), used in pre-plating heating (5 vol% H 2 +N 2 ). In particular, the heating before electroplating in No. 12 is in a combustion atmosphere containing 1 vol% oxygen up to 600 ℃ and above 600 ℃ (10 vol% H 2 +N 2 ) atmosphere.
[0131] ·Galvanizing conditions
[0132] Bath temperature: 470°C
[0133] Inserted steel plate temperature: 470°C
[0134] Al content: 0.14% by weight
[0135] Coating weight: 50g / m 2 (per surface)
[0136] Hot dip plat...
Embodiment 2
[0149]Slabs with various compositions shown in Table 3 were heated to 1200°C and hot-rolled at a finish rolling temperature of 850-900°C to obtain hot-rolled steel sheets with various thicknesses, then pickled, and then compressed The ratio is 50-68% cold rolling to obtain a cold-rolled steel sheet with a thickness of 1.2mm, which is treated under the conditions shown in Table 4 through recrystallization annealing-pickling-heating before electroplating-hot dipping, and described as follows . Particularly in No. 24 (Steel R), the hot-rolled steel sheet (thickness 1.5 mm) was pickled and treated by recrystallization annealing-pickling-heating before plating-hot-dipping without cold rolling.
[0150] In addition, as the treatment atmosphere, recrystallization annealing was used (7vol%H 2 +N 2 ), used for heating before plating (5 vol% H 2 +N 2 ). In particular, the heating before electroplating of No. 25 is in a combustion atmosphere containing 1 volume % oxygen up to 600 ° ...
PUM
Property | Measurement | Unit |
---|---|---|
tensile strength | aaaaa | aaaaa |
tensile strength | aaaaa | aaaaa |
strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com