Bakelite pen tongue and preparation method thereof

A pen tongue and bakelite technology, applied in the field of pen making, can solve problems such as poor wettability, and achieve the effects of improving elasticity, reducing production costs, and improving mechanical properties

Pending Publication Date: 2022-03-22
ZHEJIANG LISHUI BLUE SKY PEN
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The object of the present invention is to provide a lower cost and improve the wettability between the surface of the feed and the ink in order to solve the existing defect of poor wettability between the feed surface and the ink and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] This embodiment provides a bakelite feed, which includes, in parts by weight: 12 parts of raw rubber No. 1 rubber, 5 parts of butadiene rubber, 10 parts of sulfur, 3 parts of bakelite powder, 2.5 parts of 46# engine oil, light 13.5 parts of calcium carbonate, 1.8 parts of carbon black, 1.8 parts of yellow petrolatum, 0.1 part of M rubber additive, 0.1 part of D rubber additive and 0.2 part of magnesium oxide.

[0034] The preparation method comprises the following steps:

[0035] 1) Mixing: Weigh yellow vaseline and carbon black according to the formula, stir evenly, add light calcium carbonate, mix evenly, and finally add it to the matrix material, then add butadiene rubber, sulfur, powder, oil and additives , to get the mixed material;

[0036] 2) Steaming material: Preheat the mixed material obtained in step 1) to 30-45°C under nitrogen protection, the steaming material temperature is 55-65°C, the pressure changes with the steaming time, and the change curve is: 0-2...

Embodiment 2

[0040] This embodiment provides a bakelite feed, comprising 18 parts by weight of No. 1 raw rubber, 10 parts of butadiene rubber, 18 parts of sulfur, 7 parts of bakelite powder, 5 parts of 46# engine oil, light carbonic acid 24 parts of calcium, 3 parts of carbon black, 3 parts of yellow petrolatum, 0.2 parts of M rubber additive, 0.2 part of D rubber additive and 0.6 part of magnesium oxide.

[0041] The preparation method comprises the following steps:

[0042] 1) Mixing: Weigh yellow vaseline and carbon black according to the formula, stir evenly, add light calcium carbonate, mix evenly, and finally add it to the matrix material, then add butadiene rubber, sulfur, powder, oil and additives , to get the mixed material;

[0043] 2) Steaming material: Preheat the mixed material obtained in step 1) to 30-45°C under nitrogen protection, the steaming material temperature is 55-65°C, the pressure changes with the steaming time, and the change curve is: 0-2h Within 2-4 hours, the...

Embodiment 3

[0047] This embodiment provides a bakelite feed, comprising 12 parts by weight of No. 1 raw rubber, 5 parts of butadiene rubber, 10 parts of sulfur, 3 parts of bakelite powder, 2.5 parts of 46# engine oil, light carbonic acid 13.5 parts of calcium, 1.8 parts of carbon black, 1.8 parts of yellow petrolatum, 0.1 part of M rubber additive, 0.1 part of D rubber additive and 0.2 part of pretreated magnesium oxide.

[0048] The preparation method comprises the following steps:

[0049] 1) Mixing: Weigh yellow vaseline and carbon black according to the formula, stir evenly, add light calcium carbonate, mix evenly, and finally add it to the matrix material, then add butadiene rubber, sulfur, powder, oil and additives , to get the mixed material;

[0050] 2) Steaming material: Preheat the mixed material obtained in step 1) to 30-45°C under nitrogen protection, the steaming material temperature is 55-65°C, the pressure changes with the steaming time, and the change curve is: 0-2h Within...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention discloses a bakelite pen tongue and a preparation method thereof. The bakelite pen tongue comprises the following components: a parent material, butadiene rubber, sulfur, a recycled powder material, an oiling agent, a filler and an additive. By using the bakelite recycled material, the problem that part of bakelite is difficult to recycle is solved, and the production cost can be reduced; by adding butadiene rubber, the elasticity, wear resistance and cold resistance of the pen tongue can be improved; by adding yellow vaseline and carbon black, the mechanical property of the pen tongue is improved, and certain blackness is provided, so that the color of the ink is not changed; by adding light calcium carbonate, the tensile strength, wear resistance and tear strength are improved, and the consistency is adjusted; the surface of the pen tongue has good ink-loving wettability, and after the surface of the pen tongue has good wettability, ink can be evenly laid on the surface, and large-particle ink falling cannot be formed.

Description

technical field [0001] The invention belongs to the field of pen production and relates to a feed, in particular to a cost-reduced and improved bakelite feed and a preparation method thereof. Background technique [0002] The pen feed refers to the bracket of the nib of the pen, which is one of the key parts of the ink pen. The main functions of the pen feed are to be beautiful, to support the nib, to provide ink, to replenish the air in the ink bag / tank, and to provide a temporary storage place for the ink produced by the change of air pressure in the ink tank. [0003] The function of the pen feed is to store excess ink and supply it to the nib. Once a large amount of ink flows out of the pen case due to air pressure and vibration, the vertical and horizontal grooves on the tongue of the pen will play the role of "blocking floods and storing water". Once the pen case is out of water, the tongue will store it again Ink continues to be supplied to the nib. [0004] The ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L9/00C08L61/14C08L91/00C08K3/04C08K3/26
CPCC08L7/00C08K2003/265C08L9/00C08L61/14C08L91/00C08K3/04C08K3/26
Inventor 黄永和
Owner ZHEJIANG LISHUI BLUE SKY PEN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap