A kind of x70m hot-rolled steel plate for thin-gauge gas transmission straight seam welded pipe and its manufacturing method

A technology of X70M, hot-rolled steel plate, applied in the field of high-strength X70M hot-rolled steel plate for natural gas transmission pipeline and its manufacturing field, can solve the problems of poor uniformity of steel plate performance, low production cost, high rolling resistance, etc., to optimize thickness, improve The effect of reducing the amount of reduction and increasing the rolling temperature

Active Publication Date: 2022-03-22
ANGANG STEEL CO LTD
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It can meet the technical requirements of X70M steel plate without subsequent off-line heat treatment, and solves the problems of large rolling resistance, high straightening resistance and poor uniformity of steel plate performance in the production process of thin gauge, high strength, and ultra-wide X70M hot-rolled steel plate. The steel plate produced has high strength, high toughness and good comprehensive properties, which can ensure the safety of natural gas transmission line pipes, and the production cost is low and the economy is good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of x70m hot-rolled steel plate for thin-gauge gas transmission straight seam welded pipe and its manufacturing method
  • A kind of x70m hot-rolled steel plate for thin-gauge gas transmission straight seam welded pipe and its manufacturing method
  • A kind of x70m hot-rolled steel plate for thin-gauge gas transmission straight seam welded pipe and its manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0029] The invention provides a X70M hot-rolled steel plate for a thin gauge gas transmission straight seam welded pipe. The thickness of the steel plate is 10-18mm; the chemical composition of the steel plate is calculated by weight percentage: C 0.05%-0.09%, Si 0.10 %~0.35%, Mn1.50%~1.80%, P≤0.020%, S≤0.015%, Nb 0.04%~0.09%, Ti 0.008%~0.0250%, Al0.015%~0.045%, Cr≤0.4%, V 0.020% ~ 0.06%, N 0.0041% ~ 0.006%, the balance is Fe and unavoidable impurities; O ≤ 0.0050% in impurities, and the total amount of other impurity elements is less than 0.05%.

[0030] A method for manufacturing X70M hot-rolled steel plates for thin-gauge gas transmission straight seam welded pipes. The production process is molten steel smelting→outside furnace refining, degassing→continuous casting→slab reheating→controlled rolling→controlled cooling→air cooling to room temperature ;details as follows:

[0031] 1) Process from molten steel smelting to continuous casting:

[0032] The raw material is pre...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to an X70M hot-rolled steel plate for a thin-gauge gas transmission straight seam welded pipe and a manufacturing method thereof. The chemical composition of the steel plate is calculated by weight percentage: C 0.05%-0.09%, Si 0.10%-0.35%, Mn 1.50 %~1.80%, P≤0.020%, S≤0.015%, Nb 0.04%~0.09%, Ti 0.008%~0.0250%, Al 0.015%~0.045%, Cr≤0.4%, V 0.020%~0.06%, N 0.0041 % to 0.006%, and the balance is Fe and unavoidable impurities; the steel plate produced by the invention is suitable for manufacturing X70M straight seam welded pipes for natural gas pipelines with a diameter of 10 to 18 mm and a wall thickness of 10 mm.

Description

technical field [0001] The invention relates to the technical field of low-carbon micro-alloy steel production, in particular to a pipe diameter of A high-strength X70M hot-rolled steel plate for a natural gas transmission pipeline with a wall thickness of 10-18 mm and a manufacturing method thereof. Background technique [0002] Pipeline transportation is the most economical, most convenient and most important transportation method for long-distance natural gas transportation. In order to reduce the construction investment and operation and maintenance costs of long-distance natural gas pipelines and improve transmission efficiency, long-distance oil and gas pipelines have always been developed in the direction of large diameter and high pressure; at the same time, in order to ensure the economy and safety of their service, some branch lines The thickness of the project steel pipe is gradually decreasing while the strength level is gradually increasing. Correspondingly, t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/06C22C38/12C22C38/14C22C38/24C22C38/38C21C1/02C21C7/072C21C7/10C21D8/02C22C33/04
CPCC22C38/02C22C38/04C22C38/12C22C38/14C22C38/06C22C38/24C22C38/38C22C38/001C22C33/04C21C1/02C21C7/072C21C7/10C21D8/0226C21D8/0263Y02P10/143
Inventor 徐海健沙孝春任毅姚震王爽康超应传涛渠秀娟
Owner ANGANG STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap