Method for inhibiting scale on surface of blunt metal material

A metal material and anti-scaling technology, which is applied in chemical instruments and methods, cleaning methods and utensils, cleaning methods using liquids, etc., can solve the problems of high cost and tediousness, and achieve high cost, broad application prospects, and anti-scaling Obvious effect

Active Publication Date: 2020-09-25
XI'AN UNIVERSITY OF ARCHITECTURE AND TECHNOLOGY
View PDF14 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to overcome the deficiencies of the above-mentioned prior art, the object of the present invention is to provide a method for inhibiting scale on the surface of passive metal materials, which has good scale inhibition effect, low cost, simple preparation, economical and practical, and can well overcome the traditional However, the scale method has the disadvantages of high cost, cumbersome, serious pollution, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for inhibiting scale on surface of blunt metal material
  • Method for inhibiting scale on surface of blunt metal material
  • Method for inhibiting scale on surface of blunt metal material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] The present invention will be described in further detail below in conjunction with the accompanying drawings.

[0023] The pretreatment involved in the specific embodiment of the present invention is as follows:

[0024] Put the sample into the organic solvent acetone or metal cleaning agent for ultrasonic cleaning to remove the oil and impurities on the surface. Finally, wash with deionized water, dry, and set aside.

[0025] After the degreasing treatment is completed, the specific surface processing steps are as follows:

[0026] First, fix the 316L stainless steel that has been degreased on the machine tool, and then set the process parameters of ultrasonic rolling processing. The main parameters are: processing line speed 2m / min, step distance 0.08mm, pressure 1MPa, pneumatic ball, rolling 5 Second-rate. Then, start the power switch, and perform ultrasonic rolling treatment on the surface of 316L stainless steel. The surface of 316L stainless steel after ultra...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for inhibiting scale on the surface of a blunt metal material. The method comprises the following steps that firstly, a sample is subjected to surface oil removal treatment; secondly, ultrasonic surface rolling machining is conducted; and finally, rolling surface protection is implemented, so that the surface of the blunt metal material is kept in the machining state for service use. The method has the advantages of favorable scale inhibition effect, lower cost and simple preparation, and can well overcome the defects of high cost, complexity, severe partial pollution and the like in the traditional scaling method.

Description

technical field [0001] The invention relates to the technical field of metal material surface treatment application, in particular to a method for inhibiting scale on the surface of passive metal materials. Background technique [0002] Scaling will inevitably occur on the surface of petroleum pipelines, heat exchangers, boilers and other equipment composed of metal materials during service. This is mainly because during the use of metal equipment, the original material balance is broken due to changes in medium temperature, pressure, components, etc., so that scale-forming ions produce crystal grains through crystallization, and grow into dirt after long-term accumulation. . Generally speaking, CaCO is the main component of the fouling 3 Mainly scale, also mixed with MgCO 3 , CaSO 4 , MgSO 4 Wait. After scaling occurs on the surface of metal equipment, if it is not cleaned in time, it will bring a series of problems. For example, after scaling occurs in oil field gath...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B23P9/02B08B3/12C23G5/032
CPCB23P9/02C23G5/032B08B3/12
Inventor 唐长斌陶冠宇薛娟琴毕强李发根尹成先
Owner XI'AN UNIVERSITY OF ARCHITECTURE AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products