Forming mold and preparation method for testing the interface fracture performance of heterogeneous concrete

A technology for forming molds and fracture properties, which is applied in the preparation of test samples, molds, and the use of stable tension/pressure to test the strength of materials, etc. It can solve the problems of difficult preparation of composite test pieces and inability to reflect the impact, and achieve low cost , the effect of simple operation

Active Publication Date: 2021-08-24
TIANJIN UNIV
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

How to consider the influence of the splitting strength of different concrete interfaces through indoor experiments is one of the research directions of hydraulic structures. At present, the splitting strength measurement molds of concrete specimens used in laboratories mostly measure a single concrete material, and it is difficult to prepare concrete with a clear interface by using the above molds. Composite specimens that can measure the splitting strength of dissimilar concrete cannot reflect the influence of the interfacial bonding effect of dissimilar concrete on the splitting strength in hydraulic structural engineering

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Forming mold and preparation method for testing the interface fracture performance of heterogeneous concrete
  • Forming mold and preparation method for testing the interface fracture performance of heterogeneous concrete
  • Forming mold and preparation method for testing the interface fracture performance of heterogeneous concrete

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] In order to make the object, technical solution and advantages of the present invention clearer, the present invention will be further described in detail below in conjunction with specific embodiments and with reference to the accompanying drawings. It should be noted that the directional terms mentioned in the embodiments, such as "up", "down", "front", "rear", "left", "right", etc., are only for referring to the directions of the drawings, not for reference. To limit the protection scope of the present invention. Throughout the drawings, the same elements are indicated by the same or similar reference numerals. Conventional structures or constructions will be omitted when they may obscure the understanding of the present invention.

[0022] According to some embodiments of the present invention, such as Figure 1A to Figure 6 As shown, a forming mold for testing the fracture performance of heterogeneous concrete interface is provided, especially a forming mold for ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
depthaaaaaaaaaa
Login to View More

Abstract

A forming mold for testing the fracture performance of dissimilar concrete interfaces and a preparation method, the forming mold comprises a base plate, two front and rear baffles, two left and right baffles, an isolation baffle and a pre-embedded plate, wherein the base plate, the front and rear baffles It is fixed perpendicular to the left and right baffles to form the forming cavity of the dissimilar concrete composite specimen. The middle of one left and right baffles is provided with a cubic protrusion extending downward from the top to the bottom plate; the two sides of the isolation baffles are respectively fixed on The opposite side of the cubic protrusion and the other left and right baffles; one side end of the embedded plate is fixed on the cubic protrusion, and the other opposite side end is suspended. The present invention also provides a method for preparing a dissimilar concrete composite specimen by using the forming mold, which has the advantages of simple operation, low cost and reusability, and can precisely control the interface position of dissimilar concrete to ensure that no material intermixing occurs at the interface position, so as to reveal The law of fracture performance of dissimilar concrete interface provides technical support for the design of dissimilar concrete structures.

Description

technical field [0001] The invention relates to the field of hydraulic structures, in particular to a forming mold and a preparation method for testing the interface fracture performance of heterogeneous concrete. Background technique [0002] The dam is the core main building in the water conservancy project, and its safety is the key to the whole project. The different parts of the dam body partition have different working conditions, and the defects caused by the differences in the "structural characteristics" and "material properties" of each part of the dam body are directly related to the quality and durability of the engineering structure. How to consider the influence of the splitting strength of different concrete interfaces through indoor experiments is one of the research directions of hydraulic structures. At present, the splitting strength measurement molds of concrete specimens used in laboratories mostly measure a single concrete material, and it is difficult ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G01N1/36G01N3/08B28B1/08B28B7/22B28B7/30B28B7/38B28B11/24
CPCB28B1/08B28B7/22B28B7/30B28B7/384B28B7/388B28B11/245G01N1/36G01N3/08G01N2001/366
Inventor 李明超张梦溪闵巧玲
Owner TIANJIN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com