Ceramic tile with bright and matte effects and preparation method thereof

A technology of ceramic tiles, bright and dumb, applied in the field of ceramic tiles, can solve the problems of poor controllability of bright and dumb effects, poor clarity of decorative patterns, etc., and achieve the effect of high fault tolerance

Active Publication Date: 2019-03-12
FOSHAN OCEANO CERAMICS
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the bright and dumb decorative effects obtained by the above methods all have the disadvantages of poor clarity of decorative patterns and poor controllability of bright and dumb effects.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A kind of preparation method of the ceramic brick with glossy-dumb effect, it comprises following processing steps:

[0025] 1) Apply top glaze on the ceramic tile green body to obtain a top glaze layer;

[0026] 2) Ink-jet printing the decorative pattern texture on the glaze layer, drying to obtain the decorative pattern texture layer;

[0027] 3) Ink-jet printing low-temperature ceramic glue with a patterned texture and a melting temperature of 900-1100° C. on the decorative pattern texture layer to obtain a low-temperature ceramic glue layer;

[0028] 4) Take glossy dry granules and matte dry granules with particle sizes ranging from 100 to 150 meshes, mix glossy dry granules and matte dry granules at a mass ratio of 1:1, and then add ceramic ink, ceramic ink and glossy dry granules The mass ratio is 1:1 to obtain bright and matte dry glaze;

[0029] 5) Spraying bright and dull dry grain glaze on the low-temperature ceramic glue layer, and drying to obtain bright a...

Embodiment 2

[0033] A kind of preparation method of the ceramic brick with glossy-dumb effect, it comprises following processing steps:

[0034] 1) Apply top glaze on the ceramic tile green body to obtain a top glaze layer;

[0035] 2) Ink-jet printing the decorative pattern texture on the glaze layer, drying to obtain the decorative pattern texture layer;

[0036] 3) Ink-jet printing low-temperature ceramic glue with a patterned texture and a melting temperature of 1050-1100° C. on the decorative pattern texture layer to obtain a low-temperature ceramic glue layer;

[0037] 4) Take glossy dry granules and matte dry granules with particle sizes ranging from 150 to 200 meshes, mix glossy dry granules and matte dry granules at a mass ratio of 1:1.5, and then add ceramic ink, ceramic ink and glossy dry granules The mass ratio is 1:1.2 to obtain bright and matte dry glaze;

[0038] 5) Spraying bright and dull dry grain glaze on the low-temperature ceramic glue layer, and drying to obtain bri...

Embodiment 3

[0042] A kind of preparation method of the ceramic brick with glossy-dumb effect, it comprises following processing steps:

[0043] 1) Apply top glaze on the ceramic tile green body to obtain a top glaze layer;

[0044] 2) Ink-jet printing the decorative pattern texture on the glaze layer, drying to obtain the decorative pattern texture layer;

[0045] 3) Ink-jet printing low-temperature ceramic glue with a patterned texture and a melting temperature of 950-1100° C. on the decorative pattern texture layer to obtain a low-temperature ceramic glue layer;

[0046] 4) Take glossy dry granules and matte dry granules with particle sizes ranging from 100 to 200 meshes, mix glossy dry granules and matte dry granules at a mass ratio of 1:1.2, and then add ceramic ink, ceramic ink and glossy dry granules The mass ratio is 1:1.1 to obtain bright and matte dry glaze;

[0047] 5) Spraying bright and dull dry grain glaze on the low-temperature ceramic glue layer, and drying to obtain brig...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a ceramic tile with bright and matte effects. The preparation method comprises the following technology steps of (1) applying surface glaze to the ceramic tile blank, so as to obtain a surface glaze layer; (2) printing decoration pattern textures on the surface glaze layer in an ink jet way, and drying, so as to obtain a decoration pattern texture layer; (3) printing a low-temperature ceramic glue with pattern texture onto the decoration pattern texture layer in an ink jet way, so as to obtain a low-temperature ceramic glue layer; (4) spraying bright and matte dry particle glaze onto the low-temperature ceramic glue layer, and drying, so as to obtain a bright and matte dry particle layer; (5) firing at high temperature, so as to obtain a finished product. The preparation method has the advantages that under the synergistic function of the low-temperature ceramic glue and the bright and matte dry particle glaze, the tolerance rate of decoration pattern textures and glue pattern textures is high, so that while the bright and matte combination effect is realized on the decoration pattern texture layer, the bright and matte combination effect is also realized on the bright and matte dry particle layer at the surface of the ceramic tile, the controllability of the bright and matte effect of the whole ceramic tile is strong, and the definition of the decoration patterns is good. The invention also discloses the ceramic tile with the bright and matte effect prepared by the preparation method.

Description

technical field [0001] The invention relates to the field of building ceramics, in particular to a ceramic brick with bright and matte effect. Background technique [0002] Architectural ceramic tiles are an inaccessible ceramic decorative material in the current home decoration. There are many types of them, such as polished tiles, glazed tiles, antique tiles and tiles, etc. The introduction of inkjet printing technology has greatly enriched the color of the surface of ceramic tiles, making glazed tiles popular in the market for a while. However, it is also because of the introduction of inkjet printing technology that the surface of ceramic tiles The homogeneity of the decorative effect is becoming more and more serious, and it is easy to cause visual fatigue. Gradually, some personalized decorative products have appeared, such as inkjet bleeding products, sinking glaze, whole body bricks and so on. On the other hand, ceramic tiles with glossy, matte or glossy decorative ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/34C04B41/86
CPCC04B33/34C04B41/5022C04B41/86
Inventor 吴洋柯善军马超倪成林田维
Owner FOSHAN OCEANO CERAMICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com