A multicomponent iron-based amorphous soft magnetic alloy

A technology of iron-based amorphous and soft magnetic alloys, applied in magnetic objects, magnetic materials, electrical components, etc., can solve the problems of poor comprehensive performance of iron-based amorphous soft magnetic alloys, difficult to industrialize production, etc., and achieve low core loss. , The effect of simplified production process and excellent comprehensive performance

Inactive Publication Date: 2019-09-17
ZHENGZHOU UNIV
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The technical problem to be solved in the present invention is that the traditional iron-based amorphous soft magnetic alloy has poor comprehensive performance and is not easy for industrial production; in order to solve the above problems, the present invention provides a multi-component iron-based amorphous soft magnetic alloy, which has high The effective permeability μ e , low coercive force H c , High saturation magnetic induction B s , and its formability is good, the preparation process conditions are loose, and the production cost is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A multicomponent iron-based amorphous soft magnetic alloy
  • A multicomponent iron-based amorphous soft magnetic alloy
  • A multicomponent iron-based amorphous soft magnetic alloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] A multi-component iron-based amorphous soft magnetic alloy, the alloy expression is Fe 78.56 Si 9.17 B 11.20 P 0.11 Ni 0.92 C 0.04 , denoted as Y-1. As a more detailed example, its preparation method includes the following steps:

[0046] (1) Ingredients: Fe with a purity of 99.9wt%, Si with a purity of 99.99wt%, FeB with a B content of 17.40wt%, FeP with a P content of 24.98wt%, Ni and C with a purity of 99.99wt% For 5wt% FeC, dosing according to the above alloy expression. Before weighing the raw materials, remove impurities such as oxide films on the surface of the raw materials with sandpaper or a grinder, and then put the Fe and Ni raw materials into a beaker filled with absolute ethanol, perform ultrasonic cleaning for 250S, and then use a blower to blow them completely dry.

[0047] (2) Melting master alloy: Put the prepared master alloy raw materials into a quartz crucible, put the alloy components with high density and low melting point on it, put the q...

Embodiment 2

[0051] A multi-component iron-based amorphous soft magnetic alloy, the alloy expression is Fe 78.29 Si 8.92 B 11.25 P 0.15 Ni 0.90 C 0.49 , denoted as Y-2. As a more detailed example, its preparation method includes the following steps:

[0052] (1) Ingredients: Fe with a purity of 99.9wt%, Si with a purity of 99.99wt%, FeB with a B content of 17.40wt%, FeP with a P content of 24.98wt%, Ni and C with a purity of 99.99wt% For 5wt% FeC, dosing according to the above alloy expression. Before weighing the raw materials, remove impurities such as oxide films on the surface of the raw materials with sandpaper or a grinder, and then put the Fe and Ni raw materials into a beaker filled with absolute ethanol, perform ultrasonic cleaning for 240S, and then use a blower to blow them completely dry.

[0053] (2) Melting master alloy: Put the prepared master alloy raw materials into a quartz crucible, put the alloy components with high density and low melting point on it, put the q...

Embodiment 3

[0057] A new type of iron-based amorphous soft magnetic alloy, the alloy expression is Fe 80 Si 8.52 B 10.41 P 0.11 Ni 0.92 C 0.04 , denoted as Y-3. As a more detailed example, its preparation method includes the following steps:

[0058] (1) Ingredients: Fe with a purity of 99.9wt%, Si with a purity of 99.99wt%, FeB with a B content of 17.40wt%, FeP with a P content of 24.98wt%, Ni and C with a purity of 99.99wt% For 5wt% FeC, dosing according to the above alloy expression. Before weighing the raw materials, remove impurities such as oxide films on the surface of the raw materials with sandpaper or a grinder, and then put the Fe and Ni raw materials into a beaker filled with absolute ethanol, perform ultrasonic cleaning for 250S, and then use a blower to blow them completely dry.

[0059] (2) Melting master alloy: Put the prepared master alloy raw materials into a quartz crucible, put the alloy components with high density and low melting point on it, put the quartz c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a multicomponent iron-based amorphous soft magnetic alloy. An expression of the alloy is FeaSibBcPdNieCf, wherein a, b, c, d, e and f are atomic percentage contents of corresponding components respectively and meet the conditions that a is 77-82, b is 3-14, c is 8-14, d is 0-0.3, e is 0-2.2, f is 0-2, and the sum of a, b, c, d, e and f is equal to 100. The multicomponent iron-based amorphous soft magnetic alloy has high saturation magnetic induction density Bs, high effective magnetic permeability [mu]e, high frequency stability, low coercivity Hc and low core loss andis good in moldability, loose in preparation technological conditions and low in production cost.

Description

technical field [0001] The invention belongs to the technical field of amorphous alloys, in particular to a multi-element iron-based amorphous soft magnetic alloy. Background technique [0002] Amorphous materials have the remarkable characteristics of green energy saving, and have excellent soft magnetic properties, low loss, which is only equivalent to 1 / 5 to 1 / 3 of silicon steel, but compared with traditional silicon steel, there are still deficiencies, the magnetic properties of silicon steel The saturation strength can reach 2T, but the typical amorphous alloy Fe 78 Si 9 B 13 The magnetic saturation intensity Bs is only 1.56T. More researchers try to increase the magnetic saturation strength of iron-based amorphous soft magnetic alloys. The design of high magnetic induction amorphous alloy composition is mostly based on: (1) increasing the content of iron element and reducing the content of non-ferromagnetic amorphous forming elements (2) adding an appropriate amoun...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01F1/153C22C45/02
Inventor 李福山杨要轩张航刘磊刘士磊王坦陈辰魏然张许行
Owner ZHENGZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com