Environment-friendly concrete material

A technology of environmentally friendly concrete and ordinary concrete, applied in the field of new building materials, can solve the problems of reduced strength and heavy weight, and achieve the effect of convenient use and light weight

Inactive Publication Date: 2018-02-23
叠彩区千牛起重设备经营部
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Generally speaking, the existing concrete materials are generally heavy in weight, and the addition and mixing of general light substances in the production process will reduce its strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] An environmentally friendly concrete material, comprising the following components:

[0018] 200 parts by weight of ordinary concrete raw materials, 30 parts by weight of crushed straw, 50 parts by weight of activated carbon, 30 parts by weight of diatomaceous earth, 10 parts by weight of carbon fiber, 1 part by weight of magnesium oxide, 1.5 parts by weight of zinc stearate, 3 parts by weight of carbon black, 0.2 parts by weight of dicumyl peroxide.

[0019] A method for manufacturing an environmentally friendly concrete material, comprising the steps of:

[0020] (a) 200 parts by weight of ordinary concrete raw materials, 30 parts by weight of crushed straw, 50 parts by weight of activated carbon, 30 parts by weight of diatomaceous earth, 10 parts by weight of carbon fiber, 1 part by weight of magnesium oxide, 1.5 parts by weight of zinc stearate, carbon black 3 parts by weight, 0.2 parts by weight of dicumyl peroxide. Mixing is carried out to obtain a homogeneous m...

Embodiment 2

[0022] An environmentally friendly concrete material, comprising the following components:

[0023] 500 parts by weight of ordinary concrete raw materials, 50 parts by weight of crushed straw, 80 parts by weight of activated carbon, 50 parts by weight of diatomaceous earth, 15 parts by weight of carbon fiber, 2 parts by weight of magnesium oxide, 4 parts by weight of zinc stearate, 5 parts by weight of carbon black, 0.8 parts by weight of dicumyl peroxide.

[0024] A method for manufacturing an environmentally friendly concrete material, comprising the steps of:

[0025] (a) 500 parts by weight of ordinary concrete raw materials, 50 parts by weight of crushed straw, 80 parts by weight of activated carbon, 50 parts by weight of diatomaceous earth, 15 parts by weight of carbon fiber, 2 parts by weight of magnesium oxide, 4 parts by weight of zinc stearate, carbon black 5 parts by weight and 0.8 parts by weight of dicumyl peroxide were mixed to obtain a uniform mixture.

Embodiment 3

[0027] An environmentally friendly concrete material, comprising the following components:

[0028] 300 parts by weight of ordinary concrete raw materials, 43 parts by weight of crushed straw, 62 parts by weight of activated carbon, 37 parts by weight of diatomaceous earth, 13 parts by weight of carbon fiber, 1.6 parts by weight of magnesium oxide, 1.8 parts by weight of zinc stearate, 4 parts by weight of carbon black, 0.6 parts by weight of dicumyl peroxide.

[0029] A method for manufacturing an environmentally friendly concrete material, comprising the steps of:

[0030] (a) 300 parts by weight of ordinary concrete raw materials, 43 parts by weight of crushed straw, 62 parts by weight of activated carbon, 37 parts by weight of diatomaceous earth, 13 parts by weight of carbon fiber, 1.6 parts by weight of magnesium oxide, 1.8 parts by weight of zinc stearate, carbon black 4 parts by weight and 0.6 parts by weight of dicumyl peroxide were mixed to obtain a uniform mixture. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an environment-friendly concrete material. The environment-friendly concrete material comprises the following components: 200-500 parts of an ordinary concrete raw material, 30-50 parts of straw shreds, 50-80 parts of active carbon, 30-50 parts of diatomite, 10-15 parts of carbon fiber, 1-2 parts of magnesium oxide, 1.5-4 parts of zinc stearate, 3-5 parts of carbon black and 0.2-0.8 part of dicumyl peroxide. The environment-friendly concrete material uses concrete and the straw shreds as base materials, achieves recycling of waste materials and has the advantages of environmental friendliness and energy conservation.

Description

technical field [0001] The invention relates to the field of new building materials, in particular to an environmentally friendly concrete material. Background technique [0002] Generally speaking, the existing concrete materials are generally heavy, and the addition and mixing of general light substances in the production process will reduce its strength. Crop straw is an inexhaustible natural resource. The resource utilization of crop straw meets the social needs of sustainable development. Therefore, the inventor tried to combine concrete with straw scraps and add more to make a new type of environmentally friendly concrete. Material. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide an energy-saving and environment-friendly environment-friendly concrete material. [0004] The technical scheme of the present invention to solve the above-mentioned technical problems is as follows: an environmentally friendly c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00
CPCC04B28/00C04B2111/00017C04B14/02C04B14/06C04B18/24C04B14/022C04B14/08C04B14/386C04B22/066C04B24/08C04B24/00
Inventor 王君阳艳华
Owner 叠彩区千牛起重设备经营部
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com