A kind of conjugated polymer for organic semiconductor and preparation method thereof

A conjugated polymer, organic semiconductor technology, used in semiconductor/solid-state device manufacturing, semiconductor devices, electric solid-state devices, etc., can solve the problem that the absorption spectrum cannot be well matched with the solar spectrum, the energy conversion efficiency is low, and the energy transfer efficiency Low problems, to achieve the effect of improving photoelectric conversion efficiency, simple structure, improving charge transport properties and stability

Active Publication Date: 2017-10-03
山东嘉驰新材料股份有限公司
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Although people have invested a lot of research on organic solar cells and achieved rapid development, the efficiency of organic solar cells has been greatly improved, but the energy conversion efficiency of organic solar cells is still lower than that of silicon solar cells. One of the reasons is that The carrier mobility of polymers is several orders of magnitude lower than that of inorganic single crystal materials
The spectral response of the currently used conjugated polymer photovoltaic materials is relatively poor, and its absorption spectrum cannot match the solar spectrum well, which is another important reason for the low energy transfer efficiency.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of conjugated polymer for organic semiconductor and preparation method thereof
  • A kind of conjugated polymer for organic semiconductor and preparation method thereof
  • A kind of conjugated polymer for organic semiconductor and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] This embodiment discloses a conjugated polymer P1 with the following structural formula:

[0048]

[0049] Among them, n=30, R 1 for C 16 h 33 , R 2 for C 10 h 21 .

[0050] The preparation process of conjugated polymer P1 is as follows:

[0051] One, have the preparation of the compound A of following structural formula:

[0052]

[0053] The preparation method of compound A comprises the steps:

[0054] 1. Under nitrogen protection, dissolve 1.32g (2.0mmol) of 2-dimethoxyphosphono-4,5-bis(hexadecyl)-1,3-dithiol (C) in 60mL of anhydrous tetrahydrofuran The solution was cooled to -78°C, and 2.0mL of 1.5M LDA (3.0mmol) cyclohexane solution was slowly added. After the addition was completed, the reaction was stirred at -78°C for 3h, and then 0.22g (1.0mmol) of benzo [1,2-b:4,5-b']dithiophene-4,8-dione (D) in 10mL anhydrous tetrahydrofuran solution for Wittig-Horner reaction, heat preservation reaction for 0.5h, return to room temperature, continue reaction ...

Embodiment 2

[0088]This embodiment discloses a conjugated polymer P2 with the following structural formula:

[0089]

[0090] Among them, n=10, R 1 for H, R 2 for C 10 h 21 .

[0091] The preparation process of conjugated polymer P2 is as follows:

[0092] One, have the preparation of the compound A of following structural formula:

[0093]

[0094] The preparation method of compound A comprises the steps:

[0095] 1. Under the protection of nitrogen, cool the solution of 0.42g (2.0mmol) 2-dimethoxyphosphono-1,3-dithiol (C) in 40mL anhydrous tetrahydrofuran to -78℃, and slowly add 2.0mL concentration It is a solution of 1.5M LDA (3.0mmol) in cyclohexane. After the addition is complete, stir and react at -78°C for 3h, then add 0.22g (1.0mmol) of benzo[1,2-b:4,5-b' ] Dithiophene-4,8-dione (D) in 10 mL of anhydrous tetrahydrofuran was subjected to Wittig-Horner reaction, kept warm for 0.5 h, then returned to room temperature, continued for 12 h, and stopped the reaction. The exc...

Embodiment 3

[0104] An organic solar cell device, using glass as a substrate, indium tin oxide (ITO) as a conductive layer, and using the conjugated polymer P1 in Example 1 as a conjugated polymer.

[0105] The structure of the organic solar battery device is: glass / ITO / PEDOT:PSS / active layer / Al, wherein ITO is indium tin oxide with a sheet resistance of 10Ω / □˜20Ω / □. PEDOT is poly(3,4-ethylenedioxythiophene), and PSS is poly(styrenesulfonic acid). The material of the active layer is a mixture, including the electron donor material based on the conjugated polymer P1 and the [6,6]phenyl-C 61 - Butyric acid methyl ester ([6,6]-phenyl-C61-butyric acid methyl ester, PCBM) is an electron acceptor material.

[0106] The fabrication process of the organic solar cell device is as follows:

[0107] After the ITO glass is ultrasonically cleaned, it is treated with oxygen-Plasma, and a PEDOT:PSS layer is coated on the ITO, where the colon ":" indicates mixing.

[0108] On the PEDOT:PSS layer, the a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a conjugated polymer used for organic semiconductors and a preparation method thereof. The general structural formula of the conjugated polymer is as follows: wherein, n is a natural number between 10 and 100; R1 is H, or C1 to C20 The alkyl group, R2 is the alkyl group of C1~C10. The conjugated polymer can be used in organic solar cell devices, organic electroluminescence devices, organic field effect transistors, organic lasers and the like.

Description

technical field [0001] The invention relates to the field of organic semiconductor materials, in particular to a conjugated polymer with photoelectric function and its preparation method and application. Background technique [0002] Organic solar cells have attracted widespread attention as a potential renewable energy source due to their incomparable advantages over inorganic solar cells, such as low cost, simple manufacturing process, light weight, and large-area flexible preparation. The performance of organic solar cells has steadily improved over the past decade, with energy conversion efficiencies approaching 10%. [0003] Although people have invested a lot of research on organic solar cells and achieved rapid development, the efficiency of organic solar cells has been greatly improved, but the energy conversion efficiency of organic solar cells is still lower than that of silicon solar cells. One of the reasons is that The carrier mobility of polymers is several or...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G61/12H01L51/30H01L51/46H01L51/54
CPCC08G61/123C08G61/126C08G2261/3244C08G2261/3243C08G2261/145C08G2261/414C08G2261/91C08G2261/92C08G2261/95H10K85/655H10K85/654Y02E10/549
Inventor 杨荣
Owner 山东嘉驰新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com