Scar sun-screening and repairing silicon gel and preparation method thereof

A silicone gel and scar technology, applied in the field of biomedicine, can solve the problem of high cost, achieve the effects of low cost, simple preparation method and remarkable effect

Active Publication Date: 2015-12-23
TIANJIN JIASHITANG SCI & TECH
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This product works well as a sunscreen for scars, but at a higher cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Scar sun-screening and repairing silicon gel and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 7

[0032] A preparation method for sunscreen repairing silicone gel for scars, comprising the steps of:

[0033] (1) get each raw material by table 1 embodiment 1;

[0034] (2) Dispersing the antioxidant substance in a solvent, heating in a water bath at 85° C., to dissolve the antioxidant substance, and obtain an antioxidant substance solution;

[0035] (3) Continue heating in a water bath at 85°C, and disperse the sunscreen agent in the antioxidant substance solution under stirring;

[0036] (4) Add the mixture obtained in step (3) into polydimethylsiloxane, stir evenly at a stirring speed of 20 rpm, and obtain a homogeneous system which is a scar sunscreen repair silicone gel.

Embodiment 8

[0038] A preparation method for sunscreen repairing silicone gel for scars, comprising the steps of:

[0039] (1) get each raw material by table 1 embodiment 2;

[0040] (2) Dispersing the antioxidant substance in a solvent, heating in a water bath at 80° C. to dissolve the antioxidant substance, and obtain an antioxidant substance solution;

[0041] (3) Continue heating in a water bath at 80°C, and disperse the sunscreen agent in the antioxidant substance solution under stirring;

[0042] (4) Add the mixture obtained in step (3) into polydimethylsiloxane, stir evenly at a stirring speed of 15 rpm, and obtain a homogeneous system that is a scar sunscreen repairing silicone gel.

Embodiment 9

[0044] A preparation method for sunscreen repairing silicone gel for scars, comprising the steps of:

[0045] (1) get each raw material by table 1 embodiment 3;

[0046] (2) Dispersing the antioxidant substance in a solvent, heating in a water bath at 83° C. to dissolve the antioxidant substance, and obtain an antioxidant substance solution;

[0047] (3) Continue heating in a water bath at 83°C, and disperse the sunscreen in the antioxidant solution under stirring;

[0048] (4) Add the mixture obtained in step (3) into polydimethylsiloxane, stir evenly at a stirring speed of 18 rpm, and obtain a homogeneous system that is a scar sunscreen repairing silicone gel.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a scar sun-screening and repairing silicon gel and a preparation method thereof. The scar sun-screening and repairing silicon gel is prepared from the following raw materials in percentage by weight: 55-90% of polydimethylsiloxane, 1-20% of a sun-screening agent, 0.2-8% of an antioxidant substance and 2-35% of a solvent. Experiments prove that the scar sun-screening and repairing silicon gel disclosed by the invention is good in sun-screening effect and is capable of inhibiting scar hyperplasia; upon clinical tests, the effective rate of repairing scars after sun exposure is more than 90.00%; the silicon gel is conducive to the protection and repairing of scars under a condition of sun exposure, and the silicon gel is capable of diluting chromatosis and taking a significant effect; and the preparation method disclosed by the invention is simple, short in production cycle, simple in prescription and low in cost.

Description

technical field [0001] The invention belongs to the technical field of biomedicine, and in particular relates to a scar sunscreen repair silicone gel which can achieve better healing effect by sunscreen, moisturizing and anti-oxidation for damaged skin. Background technique [0002] As early as 1983, Perkin et al. added a silicone gel film between the elastic band and the scar to prevent direct friction when using the elastic band to compress the scar, and found that the effect was much better than that of the elastic band alone. Thus uncovered the inhibitory effect of silicone gel on scars and has received extensive attention. [0003] Studies have pointed out that silicone gel has the effect of treating scars because silicone gel can form a layer of silicone gel film after being applied to damaged skin, which can slowly and continuously release silicone oil, and silicone oil helps to separate necrotic tissue , Accelerate the proliferation of granulation tissue and the for...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61K8/97A61K8/67A61K8/02A61Q17/04A61Q19/00A61Q19/02
Inventor 丁利营张珂珂王倩王卉李俊明陈凯凯
Owner TIANJIN JIASHITANG SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com