Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A kind of preparation method of polycarboxylate water reducer

A technology of water reducer and polycarboxylate, which is applied in the field of preparation of polycarboxylate water reducer, can solve the problems of high energy consumption, increased production cost, high pollution, etc., and achieve low equipment investment, stable product performance, and easy operation easy effect

Inactive Publication Date: 2018-02-09
佛山柯杰科技实业有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] The purpose of the present invention is to provide a preparation method of polycarboxylate water reducer, which can overcome the high energy consumption and high pollution of synthetic polycarboxylate water reducer, resulting in the increase of production cost products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of polycarboxylate water reducer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] a Prepare the configuration of the initiator

[0023] Add 100g of vitamin C to the container, add water to dissolve, then add 1g of trisodium phosphate and 80g of sodium allyl sulfonate, continue to add water to dissolve, and configure it into a Y solution with a mass concentration of 5%. Store them for 7 days, 15 days, 30 days, and 50 days respectively, and mark them as Y1-1, Y1-2, Y1-3, and Y1-4.

[0024] b Initiator initiates synthesis of polycarboxylate superplasticizer

[0025] Add 500g of allyl polyoxyethylene ether to the reaction vessel, add 2500g of water at the same time, stir at room temperature until completely dissolved, then add 1g of hydrogen peroxide, 50g of acrylic acid, and 5g of Y solution, and then continue to stir and react for 1.0 hours, using a mass concentration of 30% The sodium hydroxide solution is adjusted to make it PH=7, and the gained transparent liquid is the target product polycarboxylic acid.

[0026] Replace Y with Y1-1, Y1-2, Y1-3, ...

Embodiment 2

[0028] a Prepare the configuration of the initiator

[0029] Add 100g of sodium bisulfite to the container, add water to dissolve, then add 5g of mercaptopropionic acid and 40g of sodium methallylsulfonate, continue to add water to dissolve, and configure it into a Y solution with a mass concentration of 7%. Store them for 7 days, 15 days, 30 days, and 50 days respectively, and mark them as Y2-1, Y2-2, Y2-3, and Y2-4.

[0030] b Initiator initiates synthesis of polycarboxylate superplasticizer

[0031] Add 500g of sodium methallyl sulfonate to the reaction vessel, add 1000g of water at the same time, stir at room temperature until completely dissolved, then add 2g of potassium oxalate, 25g of lactic acid, and 8g of Y solution, and then continue to stir and react for 1.5 hours.

[0032] Use a sodium hydroxide solution with a mass concentration of 40% to adjust the pH to 6, and the resulting transparent liquid is the target product polycarboxylic acid.

[0033] Replace Y with ...

Embodiment 3

[0035] a Prepare the configuration of the initiator

[0036] Add 100g of hanging white cubes to the container, add water to dissolve, then add 1.5g of thioglycolic acid, 60g of 2-acrylamido-2 methylpropanesulfonic acid, continue to add water to dissolve, and configure it to a mass concentration of 10%. solution. Store them for 7 days, 15 days, 30 days, and 50 days respectively, and mark them as Y3-1, Y3-2, Y3-3, and Y3-4.

[0037] b Initiator initiates synthesis of polycarboxylate superplasticizer

[0038] Add 500g of allyl polyoxyethylene ether to the reaction vessel, add 1500g at the same time, stir at room temperature until completely dissolved, then add 2g of hydrogen peroxide, 40g of maleic anhydride, and 6g of Y solution, and then continue to stir for 1.5 hours. % sodium hydroxide solution is adjusted to make it PH=6, and the gained transparent liquid is the target product polycarboxylic acid.

[0039] According to the above, replace Y with Y3-1, Y3-2, Y3-3, Y3-4 resp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A preparation method of a polycarboxylate water reducer, the method comprises the steps of: adding 2-5 times the weight of unsaturated polyether to stirring and dissolving water, adding an oxidizing agent, a catalyst and an initiator respectively thereto, and then continuing to stir and react for 1.0 ‑1.5 hours, adjust its PH=6‑7, the resulting transparent liquid is the target product; the mass ratio of unsaturated polyether to catalyst is 10:(0.5‑1); the mass ratio of unsaturated polyether to oxidant is 500:( 1-2); the mass ratio of unsaturated polyether to initiator is 500:(5-8); wherein, the oxidizing agent is one of hydrogen peroxide and potassium permanganate, potassium oxalate, potassium chromate, ammonium persulfate or A mixture of at least two; the catalyst is one or a mixture of at least two of acrylic acid, methacrylic acid, maleic anhydride, lactic acid, and unsaturated esters. The technical process of the invention is simple and convenient to operate, less equipment investment is required, and the synthesized product has stable performance.

Description

technical field [0001] The invention relates to the field of concrete admixtures, in particular to a preparation method of a polycarboxylate water reducer. Background technique [0002] With the acceleration of social modernization, the demand for concrete is increasing year by year, and higher requirements are placed on the performance of concrete: high fluidity, high compression resistance, high durability and other properties are gradually improving, and the water reducing agent industry is also Invisibility is a new opportunity for development. [0003] Traditional naphthalene-based water reducers, sulfamic acid-based water reducers and aliphatic water reducers are about to withdraw from water reducers due to their performance as water reducers and the factors of high energy consumption and high pollution in the production process. The market is gradually replaced by polycarboxylate superplasticizers. [0004] The synthetic raw materials of polycarboxylate superplastic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F283/06C04B24/26C04B103/30
Inventor 许永东
Owner 佛山柯杰科技实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com