Production process of carbon fiber composite aircraft with steps on the inner wall of the shell

A composite material and production process technology, applied in the field of carbon fiber composite aircraft production process, can solve the problems of high cost, complex mold design, inability to produce the inner wall of the shell, etc., and achieve the effect of precise processing size and high production efficiency

Active Publication Date: 2016-02-17
佛山市铭特铝业科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The compression molding process uses the forming furnace to pressurize and heat the mold, and pressurizes and heats the product to be formed through the mold to realize the molding of the product. figure 1 It includes processing steps such as drawing confirmation, mold design and manufacturing, material preparation, yarn cutting, coil forming, molding, trimming and cutting, gluing, soil filling and coating, etc. However, the molding process is not suitable for production. For products with thick walls and very light weight, using this molding process to produce a carbon fiber composite aircraft with steps on the inner wall of the outer shell has complex mold design and high cost, and it may even be impossible to produce the above-mentioned carbon fiber composite aircraft with steps on the inner wall of the outer shell
Another molding process is the nylon air bag air pressure molding process, which uses the molding furnace to pressurize and heat the mold. The high-pressure gas enters the nylon air bag through the gas nozzle and applies pressure to the product from the inner cavity of the product. At the same time, the molding furnace heats the mold to realize the product. Forming, the processing steps are basically the same as the compression molding process, and the difference between the compression molding process and the compression molding process is mainly to increase the air duct step in the coil forming stage, that is, to put the air duct into the product cavity in advance, but the above-mentioned nylon air bag air pressure molding process cannot Production of carbon fiber composite aircraft with steps on the inner wall of the shell, the step form of the above-mentioned carbon fiber composite aircraft with steps on the inner wall of the shell is as follows: image 3 The gluing step of the motor fixing plate on the aircraft shown includes the motor fixing plate body 1 and the step 10
[0003] In order to solve the above-mentioned existing two kinds of molding processes, it is impossible to produce the shell inner wall with such as attached image 3 The technical problems of the carbon fiber composite aircraft with the steps shown above are in urgent need of a solution that can realize the molding production of the above-mentioned carbon fiber composite aircraft with steps on the inner wall of the shell while ensuring the strength, processing accuracy and production efficiency of the molded product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production process of carbon fiber composite aircraft with steps on the inner wall of the shell
  • Production process of carbon fiber composite aircraft with steps on the inner wall of the shell
  • Production process of carbon fiber composite aircraft with steps on the inner wall of the shell

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] In the following, the present invention will be further described in conjunction with the accompanying drawings and specific embodiments, so as to understand more clearly the technical idea claimed in the present invention.

[0025] The production process of the carbon fiber composite aircraft with steps on the inner wall of the shell of the present invention, as attached figure 2 The process steps shown include confirmation of drawings, design of silicone liner, mold design and manufacture, filling of silicone liner, material preparation, yarn cutting, roll forming, molding, trimming and cutting, gluing, soil filling and coating, and specific processes Proceed as follows:

[0026] Step 1, drawing confirmation, process analysis according to the product drawing, evaluate whether each part of the product drawing is suitable for process production, such as rounded corners, dimensions, etc., if there are parts that are not suitable for process production, modify the produc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a production process of an aircraft made from a carbon fiber composite material with steps at the inner wall of a shell. The production process comprises the processing steps of confirming drawings, designing a silica gel inner container, designing and producing a mould, casting the silica gel inner container, preparing materials, cutting yarns, rolling the materials and forming, molding, trimming deflashing, cutting and processing, gluing, compensating soil and coating. The working procedures of designing and producing the silica gel inner container are increased on the basis of an existing compression molding process, the product is extruded by utilizing the expansion of the silica gel inner container after being heated to realize the molding of the aircraft made from the carbon fiber composite material with steps at the inner wall of the shell, after molding, and the silica gel inner container is taken out when the mould is cooled and the silica gel inner container is contracted after being cooled to obtain a finished product of the aircraft made from the carbon fiber composite material with steps at the inner wall of the shell. The production process disclosed by the invention can be used for overcoming the defects of the existing compression molding process and an air pressure molding process of a nylon air bag, and has the advantages of high production efficiency, high strength and good appearance of molded products, precise machining size and the like.

Description

technical field [0001] The invention belongs to the technical field of carbon fiber composite material aircraft molding, and in particular relates to a production process of a carbon fiber composite material aircraft with steps on the inner wall of the casing. Background technique [0002] Conventional carbon fiber composite aircraft with uniform wall thickness and no steps on the inner wall can generally be formed by compression molding or nylon airbag air pressure molding. The compression molding process uses the forming furnace to pressurize and heat the mold, and pressurizes and heats the product to be formed through the mold to realize the molding of the product. figure 1 It includes processing steps such as drawing confirmation, mold design and manufacturing, material preparation, yarn cutting, coil forming, molding, trimming and cutting, gluing, soil filling and coating, etc. However, the molding process is not suitable for production. For products with thick walls a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B29C43/10B29C33/38
Inventor 刘巧练
Owner 佛山市铭特铝业科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products