Gold pigment for colored glazes and application method of gold pigment
An application method and golden technology, applied in the field of glaze preparation, can solve problems such as change, inability to express product characteristics, single color, etc., and achieve the effects of easy realization, vivid process effects, and simple and easy application methods.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0014] 80KG sodium hydroxide, 117KG quartz sand, 2KG borax, 16KG sodium nitrate, 1KG china clay, 0.5KG sodium fluorosilicate, 2KG antimony oxide, 18KG calcium carbonate, 1KG potassium carbonate, 1KG barium carbonate, 90 grams of 99.99% content After the gold is mixed evenly, it is melted at a temperature of 1400 degrees for 18 hours to form a liquid state, which is obtained by water quenching (that is, after cooling by water cooling), drying, crushing, and passing through a 120-mesh sieve.
[0015] The application method of the gold pigment for colored glaze is to sprinkle the gold pigment evenly on the iron plate for use, then take the crystal material with an iron rod, and roll it on the gold pigment at a uniform speed, so that the gold pigment evenly covers the The surface of the crystal material is then rolled over the prepared 0.5mm sterling silver paper, after tempering, and finally a layer of crystal material is put on the outside of the gold pigment to form it, and fina...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com