Zero-halogen flame-retardant thermoplastic polyurethane elastomer sheath material and preparation as well as application thereof

A technology of thermoplastic polyurethane and sheath material, applied in the direction of conductors, insulated conductors, electrical components, etc., can solve the problems of high price, narrow processing temperature, etc., and achieve the effect of wide extrusion processing temperature and strong physical and mechanical properties

Inactive Publication Date: 2013-01-02
SHANGHAI KAIBO SPECIAL CABLE FACTORY
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, thermoplastic polyurethane elastomers also have some shortcomings, such as too narrow processing temperature, high price, and the oxygen index of polyurethane elastomer itself is only 18, which is a flammable material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Zero-halogen flame-retardant thermoplastic polyurethane elastomer sheath material and preparation as well as application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Polyurethane, halogen-free flame retardant, halogen-free smoke suppressant, processing modifier, processing aid, antioxidant and anti-ultraviolet agent, have the formula shown in Table 1, and the properties are shown in Table 2.

[0027] Table 1

[0028] raw material name

parts by weight

Polyurethane WHT-7185

60

trihydroxyhexyl cyanurate

15

Zinc borate

15

Acrylonitrile-styrene-butadiene copolymer

10

Magnesium stearate

0.2

Antioxidant KY-1076

0.2

UV-531

0.2

[0029] Preparation method: use polyurethane base material, add halogen-free flame retardant, halogen-free smoke suppressant, processing modifier, processing aid, antioxidant and anti-ultraviolet agent according to weight ratio, mix evenly, and extrude through twin-screw out of granulation. The temperature setting of the twin-screw extruder is: 140±5°C in barrel I zone, 150±5°C in barrel II zone, 160±5°C ...

Embodiment 2

[0033] Polyurethane, halogen-free flame retardant, halogen-free smoke suppressant, processing modifier, processing aid, antioxidant and anti-ultraviolet agent, have the formula shown in Table 3, and the properties are shown in Table 4.

[0034] table 3

[0035] raw material name

parts by weight

Polyurethane WHT-7185

55

[0036] FR-600

15

Zinc borate

15

Acrylonitrile-styrene-butadiene copolymer

15

Magnesium stearate

0.2

KY-1076

0.2

UV-531

0.2

[0037] Preparation method: use polyurethane base material, add halogen-free flame retardant, halogen-free smoke suppressant, processing modifier, processing aid, antioxidant and anti-ultraviolet agent according to weight ratio, mix evenly, and extrude through twin-screw out of granulation. The temperature setting of the twin-screw extruder is: 140±5°C in barrel I zone, 150±5°C in barrel II zone, 160±5°C in barrel II...

Embodiment 3

[0041] Polyurethane, halogen-free flame retardant, halogen-free smoke suppressant, processing modifier, processing aid, antioxidant and anti-ultraviolet agent, have the formula shown in Table 5, and the properties are shown in Table 6.

[0042] table 5

[0043] raw material name

parts by weight

Polyurethane WHT-7185

60

FR-600

20

[0044] magnesium hydroxide

10

Ethylene acrylic acid copolymer

10

Zinc stearate

0.2

KY-1076

0.2

UV-531

0.2

[0045] Preparation method: use polyurethane base material, add halogen-free flame retardant, halogen-free smoke suppressant, processing modifier, processing aid, antioxidant and anti-ultraviolet agent according to weight ratio, mix evenly, and extrude through twin-screw out of granulation. The temperature setting of the twin-screw extruder is: 140±5°C in barrel I zone, 150±5°C in barrel II zone, 160±5°C in barrel III zone,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
oxygen indexaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a zero-halogen flame-retardant thermoplastic polyurethane elastomer sheath material and a preparation method thereof. The zero-halogen flame-retardant thermoplastic polyurethane elastomer sheath material is prepared from the following raw material components in parts by weight: 50-80 parts of polyurethane, 10-30 parts of zero-halogen flame retardant, 10-20 parts of zero-halogen smoke suppressant, 5-20 parts of processing modifier, 0.2+ / -0.05 part of processing auxiliary agent, 0.2+ / -0.05 part of antioxidant and 0.2+ / -0.05 part of ultraviolet resistant. Compared with the prior art, the zero-halogen flame-retardant thermoplastic polyurethane elastomer sheath material prepared by the invention has the advantages of wider processing temperature range, ultrahigh physical and mechanical properties and flame retardant property of UL-94 and V-0 level.

Description

technical field [0001] The invention relates to a halogen-free flame-retardant thermoplastic polyurethane elastomer sheath material and its preparation and application. Background technique [0002] Thermoplastic polyurethane elastomers have been in existence for decades, and have developed rapidly in recent years. The performance of thermoplastic polyurethane elastomers is very superior, and they have sufficient resistance to oxygen, ozone and radiation, etc., and have high tensile strength. And elongation at break, as well as good abrasion resistance, oil resistance and cold resistance, these properties make thermoplastic polyurethane elastomers a place for cable materials in some demanding environments. However, thermoplastic polyurethane elastomers also have some shortcomings, such as too narrow processing temperature, high price, and the oxygen index of polyurethane elastomer itself is only 18, which is a flammable material. Due to the particularity of this industry, t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L75/04C08K13/02B29B9/06H01B7/295
Inventor 陈进明汪晓明
Owner SHANGHAI KAIBO SPECIAL CABLE FACTORY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com