Process for partitioning and three-dimensional material distribution of ceramic tiles

A vitrified brick and three-dimensional technology, which is applied in the field of vitrified brick partitioned three-dimensional fabric technology, can solve the problems of not well reflecting the natural and smooth effect of natural stone, mechanical and rigid pattern characteristics, and achieves a wide range of designs and realistic effects. , Controllable effect

Active Publication Date: 2012-05-16
JIANGXI CIMIC CERAMICS +2
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, in the market of vitrified tile products, there are many imitation granite products. Some of these products use single-zone flat fabrics to add line technology, and some use large particles and point bleeding. The product pattern characteristics are mechanical and rigid, which cannot be very good. Reflect the natural smooth effect of natural stone

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process for partitioning and three-dimensional material distribution of ceramic tiles
  • Process for partitioning and three-dimensional material distribution of ceramic tiles
  • Process for partitioning and three-dimensional material distribution of ceramic tiles

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Such as figure 1 Shown; a vitrified brick divisional three-dimensional cloth process, the process includes A-area fabric delivery, B-area fabric delivery, thread material delivery and combined accumulation, the A-area fabric delivery is to place the micro-powder fabric in four fabric hoppers In 5, the four fabric rollers 6 below the fabric hopper 5 are rotated and dropped onto the conveyor belt 3, and the conveyor belt 3 moves to send the fabric into the fabric storage hopper 4, and the outlet below the storage hopper 4 is provided with a conveyor belt 2, and the conveyor belt 2 Rotate to evenly spread the micropowder fabric on the conveyor belt 2, and the front and bottom of the conveyor belt 2 are suspended in the air. The wire material conveying is to rotate the wire material 7 from the wire unloading drum 8 and drop it onto the vibrating screen 11. The vibrating screen 11 is suspended in parallel at 0 degrees, and the inclined baffle plate 12 is connected underneath...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a process for partitioning and three-dimensional material distribution of ceramic tiles. The process comprises partitioned facing material conveying and line material conveying, wherein for the partitioned facing material conveying, a micro-powder facing material is polished and then added into facing material hoppers of an area A and an area B respectively, the facing material in the area A falls into a facing material storage hopper through the rotation of a roller below the facing material hopper, the facing material storage hopper and an outlet below the facing material hopper of the area B are provided with a conveying belt, the front and the blow of the conveying belt are hung in the air, and the conveying belt rotates to convey the facing material to a stacking flat plate below the conveying belt; and for the line material conveying, a line material falls onto a baffle plate and a vibrating screen through the rotation of line blanking roller, the vibrating screen scatters the line material to the stacking flat plate below the vibrating screen thinly and uniformly, the stacking flat plate moves to partition and three-dimensionally distribute the facing material and the line material, and then a fidelity grizzly screen is used for conveying the materials to a die cavity of a pressing machine to finish the pressing of tile blanks. Compared with theprior art, the process has the advantages of texture lines naturally and smoothly added in the ceramic tiles, vivid imitation of granite, strong controllability and the like.

Description

technical field [0001] The invention relates to vitrified bricks, in particular to a vitrified brick partition three-dimensional cloth technology. Background technique [0002] At present, in the market of vitrified tile products, there are many imitation granite products. Some of these products use single-zone flat fabrics to add line technology, and some use large particles and point bleeding. The product pattern characteristics are mechanical and rigid, which cannot be very good. It perfectly embodies the natural and smooth effect of natural stone. Contents of the invention [0003] The purpose of the present invention is to overcome the defects of the above-mentioned prior art and provide a vitrified tile partition with a transparent effect similar to polycrystalline, with texture lines added naturally and smoothly, realistic imitation of granite, and strong controllability Three-dimensional cloth technology. [0004] The purpose of the present invention can be achie...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B28B3/00B28B13/02
Inventor 李慈雄
Owner JIANGXI CIMIC CERAMICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com