Special metal organic salt monomer for liquid stabilizer and preparation method thereof

A liquid stabilizer and organic salt technology, which is applied in the field of metal organic salt monomer and its preparation, can solve the problems of difficult operation control, complicated process, difficult technology popularization and product popularization, etc.

Inactive Publication Date: 2016-01-13
杭州三叶新材料股份有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these technologies have the same problems when they are implemented: first, the process is too complicated and the operation is extremely difficult to control; second, although high-content and high-purity monomers can be prepared, the production cost is too high, and it is difficult to popularize technology and products. Limiting the speed of development of the plastics industry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Special metal organic salt monomer for liquid stabilizer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0088] Calcium monomer synthesis, wherein the calcium content is between 10% and 14%. The specific process is: first add 123kg of oleic acid, 200kg of 25# transformer oil, 160kg of isodecyl alcohol, 50kg of diethylene glycol monobutyl ether, three 7kg of ethylene glycol, 1kg of propionic acid and 30kg of water; under the protection of nitrogen, start the stirring device and raise the temperature to 80°C, and evenly add: 250kg of 25# transformer oil, 80kg of neodecanoic acid, 100kg of isodecanol, A mixture composed of 50kg of ethylene glycol monobutyl ether and 350kg of calcium hydroxide; then pass carbon dioxide, the rate is controlled at 45 liters / hour, after 4 hours of reaction, the temperature is raised to 95°C; the carbon dioxide is turned off, the temperature is raised to 150°C, vacuum dehydration, adding An appropriate amount of filter aid is used to filter the reactant by suction filtration to obtain a transparent and clear amber overbased oleic acid / calcium carbonate li...

Embodiment 2

[0090] Synthesis of zinc monomer, in which the zinc content is between 10% and 14%. The specific process is: sequentially add 400kg of isooctanoic acid, 600kg of oleic acid, 150kg of lauric acid, 350kg of p-tert-butylbenzoic acid, 75kg of benzoic acid, and dipropylene glycol 20kg of methyl ether, start stirring, put in 300kg of zinc oxide after 5 minutes; then raise the temperature to 95°C, react for 2 hours, raise the temperature to 125°C, and react for 0.5 hours; after vacuum dehydration, add 400kg of phosphite, and stir at 105°C Cool down to normal temperature after 1 hour, take a sample and analyze the zinc metal content, put it into a storage tank for standby, adjust the amount of solvent as needed to obtain the monomer with the required zinc metal content.

Embodiment 3

[0092] Magnesium monomer synthesis, wherein the magnesium content is between 4% and 10%. The specific process is: sequentially add 80kg of dipropylene glycol methyl ether, 50kg of tripropylene glycol, 280kg of nonylphenol, and 260kg of isooctanoic acid; under nitrogen protection, Start stirring, put in 100kg of magnesium hydroxide 5 minutes later, and put in evenly within 15 minutes; continue to stir for 15 minutes, raise the temperature to 135°C, and remove water at the same time; Short time; the end point temperature is controlled at about 180°C, the water content is less than 0.3%, cooled to 120°C, and filtered to obtain the finished product. After sampling and analyzing the content of magnesium metal, put it into a storage tank for standby use, adjust the amount of solvent as needed to obtain a monomer with the required content of magnesium metal.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a metal organic salt monomer used as liquid stabilizer and a preparation method thereof, wherein the monomer is any one or an any-proportion composite of more than one kinds of peralkalic alkaline metal phenolate (RO)2M.XMCO3, peralkalic alkaline metal carbonate, (RO)(RCOO)2M.XMCO3 and peralkalic alkaline metal carboxylate (RCOO)2M.XMCO3. The preparation method is that: phenol is used as a dispersion phase, higher alcohol (fatty alcohol with a more than 12 carbon atoms) as active agent, and monohydric phenol with RO group and monocarboxylic acid with RCOO group are reacted with alkalic metal compound, and the acidic gas takes participate in the reaction under the temperature condition of 60 to 135 DEG C, the reaction time is controlled, and the monomer can be prepared within 3 to 6 hours; finally peralkalic liquid organic monomer with high content of Ca, Zn, Mg or Ba are prepared. The monomer is characterized by good stability and excellent lubrication effect, etc.

Description

technical field [0001] The invention relates to a chemical raw material, in particular to a special metal organic salt monomer for a liquid stabilizer and a preparation method thereof. Background technique [0002] At present, the production technology of calcium-zinc composite stabilizer in our country is still in the research and development stage. The common method is to use organic carboxylic acid as raw material and use saponification-metathesis process or direct oxidation process to mix alkaline earth metals such as barium, calcium, magnesium or zinc, magnesium, aluminum Such as metal oxide reaction synthesis, the liquid monomer prepared by this method has the problem that the metal content cannot be increased, such as calcium<6%, zinc<12%, magnesium<5%, barium<16%, etc., so compounding The resulting monomer has poor stability and low lubricity, and its transparency, weldability (ie, secondary adhesion) and other properties are not ideal. The United States...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C07C51/41C07C37/66C01F11/18C08K5/09
Inventor 施珣若胡奋奋
Owner 杭州三叶新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com