Pigment Yellow 139 or its derivatives wrapped in thermoplastic resin, its preparation method and its downstream products
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of thermoplastic resin, pigment yellow, applied in the field of pigments
Active Publication Date: 2021-06-01
DONGGUAN UNIV OF TECH
View PDF7 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
In addition, the EP424759 mentioned in this patent also uses a large amount of alcohol and alkali, and a large amount of waste liquid will still be produced after the reaction
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
preparation example Construction
[0031] The preparation method of the thermoplastic resin-wrapped pigment yellow 139 or its derivatives of one embodiment, comprises the following steps:
[0032] Mix 1,3-diiminoisoindoline compounds, cyclic compounds containing meta-diketones, solid organic acids and thermoplastic resins, and extrude or knead to obtain Pigment Yellow 139 or its derivatives wrapped in thermoplastic resins things.
[0033] Wherein, the structure of 1,3-diiminoisoindoline compounds is shown in formula (I):
[0034] R1, R2, R3, and R4 are each independently H, halogen, C1-C4 alkyl or alkoxy.
[0035] The structure of the cyclic compound containing meta-diketone is shown in formula (II):
[0036] X are independently CH 2 Or NH, Y is C=O, S, CR5R6 or NR7, R5, R6, R7 are independently H, methyl, ethyl or benzyl.
[0037] Further, the cyclic compound containing meta-diketone is selected from one of the following compounds:
[0038] The definitions of R5, R6 and R7 are the same as above.
...
Embodiment 1
[0071]
[0072] Mix (20g, 138mmol) 1,3-diiminoisoindoline, (35g, 276mmol) barbituric acid, (6.6g, 34mmol) citric acid and 0.5kg of PMMA in a single-screw extruder Extrusion reaction, pelletizing, to obtain crude color masterbatch.
[0073] figure 1 The reflectance spectrogram of injection molding into sheet after mixing ABS for the color masterbatch crude product prepared in embodiment 1, by figure 1 It was found that the obtained plastic sheet was yellow.
Embodiment 2
[0075] Mix (20g, 138mmol) 1,3-diiminoisoindoline, (35g, 276mmol) barbituric acid, (6.6g, 34mmol) citric acid and 0.5kg of PP in a single-screw extruder Extrusion reaction, pelletizing, to obtain crude color masterbatch.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
particle diameter
aaaaa
aaaaa
particle diameter
aaaaa
aaaaa
Login to View More
Abstract
The application relates to thermoplastic resin-wrapped pigment yellow 139 or its derivatives, its preparation method and its downstream products. The method mixes 1,3-diiminoisoindoline compounds, cyclic compounds containing meta-diketones, solid organic acids and thermoplastic resins, and adjusts the amount of each raw material, and then utilizes the thermoplastic resin as a reaction dispersion medium. The good processing performance and other related physical properties of the resin enable their mixture to be extruded or kneaded to obtain Pigment Yellow 139 or its derivatives wrapped in thermoplastic resin in one step, because in the process of extrusion or kneading, Pigment Yellow 139 or its derivatives The product can be directly generated and evenly distributed in the thermoplastic resin, without adding any solvent during the reaction, and without separation and purification after the reaction, avoiding the generation of three wastes, greatly simplifying the process and reducing energy consumption.
Description
technical field [0001] The invention relates to the technical field of pigments, in particular to thermoplastic resin-wrapped pigment yellow 139 or its derivatives, its preparation method and its downstream products. Background technique [0002] C.I. Pigment Yellow 139, also known as Isoindoline Yellow, or Permanent Yellow 3R 1819, is a high-performance organic yellow pigment with strong tinting strength and good fastness. It is widely used in the coloring of printing inks and plastic products, especially Some high-performance industrial products. Usually, Pigment Yellow 139 is prepared by condensation reaction. 1,3-diiminoisoindoline and barbituric acid are reacted and filtered at 60°C to form crude Pigment Yellow 139 in an aqueous solution containing formic acid. The pure product of Pigment Yellow 139 can be obtained by recrystallization. Although the thermal stability limit temperature of Pigment Yellow 139 is 260°C, the stability of Pigment Yellow in plastic processin...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More