Composite activated carbon filter element and preparation method thereof

A technology of composite activated carbon and coconut shell activated carbon, applied in chemical instruments and methods, other chemical processes, water/sludge/sewage treatment, etc., can solve problems such as uneven water quality, loss of adsorption function, and large differences in impurity components , to prolong the effective use time, improve the adsorption efficiency, and achieve the effect of pure water taste

Inactive Publication Date: 2017-09-19
KAMFORD CHINA CO LTD
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, ordinary activated carbon fibers are easy to saturate, poor in strength, dusty, and the adsorption capacity will decrease with the use time, resulting in uneven water quality; after a short period of use, the adsorption function will be lost, and it needs to be replaced frequently, which is expensive
At the same time, due to the different quality of domestic raw water and the large difference in impurity components, pure activated carbon fibers cannot be absorbed thoroughly for a long time, resulting in certain limitations in its application range.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite activated carbon filter element and preparation method thereof
  • Composite activated carbon filter element and preparation method thereof
  • Composite activated carbon filter element and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0042] The present invention provides the preparation method of the composite activated carbon filter element described in the above technical scheme, comprising the following steps:

[0043] (1) each component that composite active carbon filter core comprises is mixed with water, obtains mixed material;

[0044] (2) Under negative pressure conditions, the mixed material in the step (1) is subjected to molding treatment to obtain a molded filter element;

[0045] (3) dehydrating the formed filter element in the step (2) to obtain a dehydrating filter element;

[0046] (4) The dehydration filter element in the step (3) is subjected to sizing treatment to obtain a composite activated carbon filter element.

[0047] The invention mixes each component contained in the composite activated carbon filter core with water to obtain a mixed material. In the present invention, the mass ratio of activated carbon fiber cloth to water in the mixed material is preferably 1:(10-20), more pre...

Embodiment 1

[0057] (1) In parts by weight, under the condition that the stirring rate is 7400 rpm, 4 parts of activated carbon fiber cloth with a fiber length of 0.5 to 1 mm, 6 parts of wood carbon, 28 parts of coconut shell activated carbon, 2 parts of acrylic glue and 60 parts of water Parts were stirred and mixed for 30min to obtain the mixed material;

[0058] (2) Transport the mixed material in the step (1) to the molding machine, wrap the cylindrical skeleton with holes on the non-woven fabric, and then insert the cylindrical skeleton covered with the non-woven fabric into the molding machine On the adsorption rod, a negative pressure of 0.097Mpa is generated by a vacuum negative pressure pump, so that the mixed material in the molding machine is evenly adsorbed on the cylindrical skeleton covered with non-woven fabric, and the adsorption time is 2s to obtain a formed filter element;

[0059] (3) Dehydrating the formed filter element in the step (2) by a vacuum negative pressure pum...

Embodiment 2

[0063] (1) In parts by weight, under the condition that the stirring rate is 7400rpm, 3 parts of activated carbon fiber cloth with a fiber length of 0.5 to 1mm, 3 parts of wood carbon, 25 parts of coconut shell activated carbon, 2 parts of acrylic glue, antibacterial agent 5 parts and 60 parts of water were stirred and mixed for 30 minutes to obtain a mixed material;

[0064] (2) Transport the mixed material in the step (1) to the molding machine, wrap the cylindrical skeleton with holes on the non-woven fabric, and then insert the cylindrical skeleton covered with the non-woven fabric into the molding machine On the adsorption rod, a negative pressure of 0.097Mpa is generated by a vacuum negative pressure pump, so that the mixed material in the molding machine is evenly adsorbed on the cylindrical skeleton covered with non-woven fabric, and the adsorption time is 2s to obtain a formed filter element;

[0065] (3) Dehydrating the formed filter element in the step (2) by a vacu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
specific surface areaaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a composite activated carbon filter element which comprises the following components in parts by weight: 3-6 parts of activated carbon fiber cloth, 3-9 parts of wood carbon, 25-32 parts of coconut shell activated carbon and 2-3 parts of acrylic glue. Adsorption properties of various carbon materials of the composite activated carbon filter element provided by the invention can supplement one another, so that the adsorption efficiency is greatly improved, and the effective use time is prolonged. Compared with a common activated carbon filter element, the composite activated carbon filter element is relatively large in adsorption specific surface area, relatively dense in structure, relatively rich in porosity, relatively high in strength, not liable to crush and relatively small in dust amount, the adsorption effect is 10 times better than that of the common activated carbon filter element and is 25 times better than that of granular activated carbon, and water purified by using the filter element is relatively pure in taste.

Description

technical field [0001] The invention relates to the technical field of water purification, in particular to a composite activated carbon filter element and a preparation method thereof. Background technique [0002] Activated carbon fiber has a developed specific surface area and narrow pore size distribution. It has the functions of absorbing different colors, odors and residual chlorine in water, and has a good removal effect. Therefore, it is widely used in water quality treatment in many fields such as food, medicine, chemical industry, and environmental protection. in process. [0003] However, ordinary activated carbon fibers are easy to saturate, poor in strength, dusty, and the adsorption capacity will decrease with the use time, resulting in uneven water quality; after a short period of use, the adsorption function will be lost, and it needs to be replaced frequently, which is expensive. At the same time, due to the different quality of domestic raw water and the l...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J20/20B01J20/30C02F1/28C02F101/12C02F101/20C02F101/36
CPCB01J20/20B01J20/3007C02F1/283C02F2101/12C02F2101/20C02F2101/36
Inventor 刘万林
Owner KAMFORD CHINA CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com