A lightweight hollow partition board

A partition board, hollow technology, applied in the direction of sustainable waste treatment, solid waste management, climate sustainability, etc., can solve the problems of high drying shrinkage, large toxic and side effects, easy cracking, etc., to achieve flexibility, environmental protection, non-toxicity , The effect of speeding up the reaction speed and good strength

Active Publication Date: 2018-05-15
CHANGSHA HAIHONG BUILDING MATERIALS
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the above-mentioned light-weight wallboard also has some shortcomings, such as high drying shrinkage, which leads to easy cracking after the wall is formed, and the difficulty in obtaining raw materials makes it costly, low in cost performance, and has relatively large toxic and side effects.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A lightweight hollow partition board

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A lightweight hollow partition wall panel comprising the following components:

[0015] Component A: solid waste residue and fly ash, cement, mineral powder, fluorine gypsum, wherein the weight percentage of each material is: solid waste residue and fly ash 60%, cement 15%, mineral powder 12%, fluorine gypsum 13%;

[0016] Component B: 45% by weight of anhydrous sodium sulfate and 55% by weight of potassium aluminum sulfate dodecahydrate;

[0017] Component C: dihydrate gypsum;

[0018] The weight ratio of components A:B:C is: 1000; 1:35.

[0019] The preparation method is as follows:

[0020] S1. Prepare solid waste residue, fly ash, cement, slag powder, and fluorogypsum in proportion and stir them evenly;

[0021] S2. Proportionally configure component B and component C and stir evenly;

[0022] S3, mixing the mixture obtained by S2 and S1 and stirring evenly;

[0023] S4. Put the dry blend prepared in S3 into a molding machine and add an appropriate amount of wa...

Embodiment 2

[0025] A lightweight hollow partition wall panel comprising the following components:

[0026] Component A: solid waste residue and fly ash, cement, mineral powder, fluorogypsum, wherein the weight percentage of each material is: solid waste residue and fly ash 62%, cement 16%, mineral powder 10%, fluorogypsum 12%;

[0027] Component B: 50% by weight of anhydrous sodium sulfate and 50% by weight of potassium aluminum sulfate dodecahydrate;

[0028] Component C: dihydrate gypsum;

[0029] The weight ratio of components A:B:C is: 1000; 0.5:45.

[0030] The preparation method is the same as in Example 1.

Embodiment 3

[0032] A lightweight hollow partition wall panel comprising the following components:

[0033] Component A: solid waste residue and fly ash, cement, mineral powder, fluorogypsum, wherein the weight percentage of each material is: solid waste residue and fly ash 57%, cement 13%, mineral powder 15%, fluorogypsum 15%;

[0034] Component B: 55% by weight of anhydrous sodium sulfate and 45% by weight of potassium aluminum sulfate dodecahydrate;

[0035] Component C: dihydrate gypsum;

[0036] The weight ratio of components A:B:C is: 1000; 2:41.

[0037] The preparation method is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of building materials and particularly discloses a lightweight hollow partition wallboard, comprising the following components: component A including in percent by weight: 57-65% of solid residue and flyash, 13-18% of cement, 10-15% of mineral powder and 12-16% of fluorine gypsum; component B including a mixture of 45-55% by weight of anhydrous sodium sulfate and 45-55% by weight of aluminum potassium sulfate dodecahydrate; component C including dihydrate gypsum; the components A, B and C have a weight ratio of 1000:0.5-2:30-50. The lightweight hollow partition wallboard is low in carbon, environment-friendly, light in weight, short in forming time, low in toxic and side effect and good in service performance.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a lightweight hollow partition wall board. Background technique [0002] With the development of science and technology and the continuous improvement of living standards, the concept of sustainable development has been deeply rooted in the hearts of the people. Specifically in the field of building materials, building materials are required to be energy-saving, environmentally friendly, lightweight, and better in use, such as mechanical strength, fire resistance, Sound insulation, moisture-proof and waterproof performance, and easy construction. Based on this, traditional building materials represented by clay brick walls are gradually being replaced by new-type extruded panels, ordinary gypsum hollow slats, high-strength water-resistant gypsum-based ecological wallboards and other lightweight wallboards. get promoted. However, the above-mentioned lightweight wallboa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/14C04B18/30
CPCY02W30/91
Inventor 黄绍龙
Owner CHANGSHA HAIHONG BUILDING MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com