Ecological health preservation Nixing pottery clay and the process of making ecological health water cups with it

A Nixing pottery and ecological technology, applied in applications, household appliances, clay products, etc., can solve problems such as reducing the firing rate of pottery teapots

Active Publication Date: 2017-09-01
钦州市百越陶艺有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although this invention effectively shortens the production cycle of Nixing pottery teapots, its firing temperature exceeds 1200°C, which will reduce the firing rate of pottery teapots

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] 1) Preparation of billets: Weigh 40 parts of Dongni, 25 parts of Xini, 9 parts of medical stone, 10 parts of Muyu stone, 8 parts of potassium feldspar, and 8 parts of albite feldspar, mix them evenly, place them for 15 days, and then follow the existing routine The plastic method is made into blanks;

[0029] 2) Body forming: the blank is made into a water cup body according to the existing conventional method;

[0030] 3) trimming: trimming the obtained green body;

[0031] 4) Drying of the green body: naturally air-dry the trimmed green body;

[0032] 5) Decorate the body: engrave and draw patterns or write characters on the dried body with a steel knife to obtain a pottery body;

[0033] 6) Firing: Send the obtained ceramic body into a kiln for one firing, first raise the temperature to 570°C at a rate of 110°C / h, then raise the temperature to 1080°C at a rate of 200°C / h, keep the heat and fire for 20 minutes, stop Kiln, cool down naturally, take out the semi-finish...

Embodiment 2

[0037] 1) Preparation of billets: Weigh 42 parts of Dongni, 21 parts of Xini, 12 parts of medical stone, 11 parts of Muyu stone, 6 parts of potassium feldspar, and 8 parts of albite feldspar, mix them evenly, place them for 20 days, and then follow the existing routine The plastic method is made into blanks;

[0038] 2) Body forming: the blank is made into a water cup body according to the existing conventional method;

[0039] 3) trimming: trimming the obtained green body;

[0040] 4) Body drying: naturally air-dry the trimmed body to obtain a pottery body;

[0041] 5) Decorate the body: engrave and draw patterns or write characters on the dried body with a steel knife to obtain a pottery body;

[0042] 6) Firing: Send the obtained ceramic body into the kiln for one firing, firstly raise the temperature to 650°C at a rate of 90°C / h, then raise the temperature to 1080°C at a rate of 200°C / h, heat-preserve and fire for 30 minutes, stop Kiln, cool down naturally, take out the...

Embodiment 3

[0046] 1) Preparation of billets: Weigh 45 parts of Dongni, 23 parts of Xini, 9 parts of medical stone, 10 parts of Muyu stone, 6 parts of potassium feldspar, 7 parts of albite feldspar, mix them evenly, place them for 18 days, and then follow the existing routine The grouting method is used to make blanks;

[0047] 2) Body forming: the blank is made into a water cup body according to the existing conventional method;

[0048] 3) trimming: trimming the obtained green body;

[0049] 4) Body drying: naturally air-dry the trimmed body to obtain a pottery body;

[0050] 5) Decorate the body: engrave and draw patterns or write characters on the dried body with a steel knife to obtain a pottery body;

[0051] 6) Firing: Send the obtained ceramic body into a kiln for one firing, first raise the temperature to 550°C at a rate of 100°C / h, and then raise the temperature to 1090°C at a rate of 230°C / h, keep the temperature and fire for 25min , stop the kiln, cool down naturally, take ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an ecological health-preserving Nixing pottery clay material and a process for making an ecological health-preserving water cup using the same. The mud is made of the following raw materials in weight ratio: Dongni 35-45, Xini 15-25, medical stone 8-12, wood fish stone 8-12, potassium feldspar 4-8, sodium feldspar Stone 4-8. The process of making ecological health-preserving water cups with the above-mentioned mud materials includes the steps of preparing blanks and firing the ceramic blanks. , 8-12 pieces of wood fish stone, 4-8 pieces of potassium feldspar, and 4-8 pieces of albite feldspar; the step of firing the ceramic body adopts a secondary firing process. The invention adopts special raw material ratio and secondary firing process, so that the trace elements in the raw materials that are beneficial to human health are released when the cup is used to hold water, and the elements and trace elements that are beneficial to human health are separated into the water body, and the The water is automatically improved to slightly alkaline water (pH 8.0-8.5).

Description

technical field [0001] The invention relates to the technical field of ceramics, in particular to an ecological health-preserving Nixing clay material and a process for making ecological health-preserving water cups with it. Background technique [0002] Nixing pottery (scientific name: purple clay pottery), its raw materials include east clay and west clay. The names of the mud are divided into east and west, because these two kinds of mud are respectively distributed on both sides of the Qin River across the urban area of ​​Qinzhou. Among them, Dongni is mainly distributed in the area east of the Qinjiang River, mostly in low-lying areas; its appearance is dense and soft, and it is soft clay, and its color is white with reddish and slightly yellow, and contains a small amount of quartz sand. Dongni plays a role in adjusting plasticity and combination in the production process of Nixing pottery. Xini is mainly distributed in the area west of Qinjiang River, and the storag...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/22C04B33/24
Inventor 姚震宇姚明
Owner 钦州市百越陶艺有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com