High-magnetic permeability thick composite induction plate and manufacturing method for same

A technology with high magnetic permeability and manufacturing method, applied in the field of composite induction plates, can solve the problems of uneven composite layer, low production efficiency and high cost, and achieve the effects of uniform product thickness, high production efficiency and low production cost

Inactive Publication Date: 2013-02-13
莱芜美澳冶金科技有限公司
View PDF21 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It solves the technical problems such as low production efficiency, high cost, serious pollution, and uneven composite layer that can only be caused by explosive composite at present, improves production efficiency, improves the quality of composite panels, reduces production costs, and solves the problem caused by explosions. pollution problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A composite induction plate with high magnetic permeability and large thickness is characterized in that the composite induction plate is composed of steel plate and aluminum plate; the thickness of the steel plate is 10mm, and the yield strength is 345Mpa; the thickness of the aluminum plate is 3mm.

[0029] The composite induction board is a steel-aluminum composite board.

[0030] The high magnetic permeability and large thickness composite induction plate is a combination of aluminum plate-steel plate-steel plate-aluminum plate, which is rolled and compounded on a rolling mill with a roll diameter of 1:1 and a synchronous large rolling force.

[0031] The steel grades used for the steel plate of the composite induction plate are: C: 0.30%, Si: 0.30%, Mn: 0.80%, P: ≤0.060%, S: ≤0.035%, other impurity elements are less than 0.25%, and the remaining elements are Fe.

[0032] Preferably, the aluminum plate is made of pure aluminum.

[0033] A method for manufacturing ...

Embodiment 2

[0042] Others are the same as embodiment 1. The difference is:

[0043] A composite induction plate with high magnetic permeability and large thickness is characterized in that the composite induction plate is composed of steel plate and aluminum plate; the thickness of the steel plate is 100mm, and the yield strength is 1000Mpa; the thickness of the aluminum plate is 30mm.

[0044] The composite induction board is a steel-aluminum composite board.

[0045] Preferably, the high-permeability and large-thickness composite induction plate is a combination of aluminum plate-steel plate-steel plate-aluminum plate, rolled and compounded on a rolling mill with a roll diameter of 1:1 and a synchronous large rolling force.

[0046] Preferably, the steel grades used for the steel plate of the composite induction plate are: C: 0.60%, Si: 0.45%, Mn: 0.50%, P: ≤0.060%, S: ≤0.035%, other impurity elements are less than 0.25%, and the rest The trace element is Fe.

[0047] Preferably, the...

Embodiment 3

[0058] Others are the same as embodiment 1. The difference is:

[0059] A composite induction plate with high magnetic permeability and large thickness is characterized in that the composite induction plate is composed of steel plate and aluminum plate; the thickness of the steel plate is 22mm, and the yield strength is 500Mpa; the thickness of the aluminum plate is 5mm.

[0060] The composite induction board is a steel-aluminum composite board.

[0061] Preferably, the high-permeability and large-thickness composite induction plate is a combination of aluminum plate-steel plate-steel plate-aluminum plate, rolled and compounded on a rolling mill with a roll diameter of 1:1 and a synchronous large rolling force.

[0062] Preferably, the steel grades used for the steel plate of the composite induction plate are: C: 0.50%, Si: 0.27%, Mn: 1.20%, P: ≤0.060%, S: ≤0.035%, other impurity elements are less than 0.25%, and the remaining The trace element is Fe.

[0063] Technical sch...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
yield strengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a composite plate and a manufacturing method, in particular to a manufacturing method for a high-magnetic permeability thick steel aluminum-steel copper composite for a linear motor. A composite induction plate is formed by compounding a steel plate and an aluminum plate or compounding the steel plate and a copper plate. The steel plate has a thickness of 10 to 100mm and yield strength of 345 to 1,000Mpa. The aluminum plate or the copper plate is 3 to 30mm thick. A low-carbon weak-strength steel and aluminum / copper composite material also can be produced. Production cost is low, production efficiency is high, and a product has a uniform thickness and high quality.

Description

technical field [0001] The invention relates to a composite induction plate, especially a high-permeability and large-thickness steel-aluminum or steel-copper composite induction plate, which is used as a secondary composite induction plate for a linear motor of a maglev train or a wheel-rail train and a manufacturing method thereof. Background technique [0002] Steel-aluminum composite panels have been widely used in equipment and facilities such as civilian cookers, radiators, and large air condensers for refrigeration in power stations. The demand is huge and is on the rise. For a long time, steel-aluminum composite products have mainly relied on imports. Through cooperation with customers, Angang has developed and trial-produced cold-rolled and hot-rolled steel strip substrates for composite use—that is, low-carbon low-strength hot-rolled and cold-rolled steel strips, with a thickness of 0.2-3mm, C≤0.17, Mn≤0.60 , Si≤0.30. Chinese patent 91106921 discloses a steel gra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H02K15/03H02K41/02B21C37/02
Inventor 董涛
Owner 莱芜美澳冶金科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com