Longquan official ware celadon glaze of the Ming Dynasty and method for manufacturing Longquan official ware celadon product of the Ming Dynasty by using glaze

A celadon and glaze technology, applied in the field of ceramic technology, can solve the problem of finding no physical evidence

Inactive Publication Date: 2010-06-16
李邦强
View PDF0 Cites 39 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

"According to historical data, the court of the Ming Dynasty fired porcelain in Longquan, Zhejiang, but no physical evidence has been found for many years.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Embodiment Longquan Ming Dynasty official kiln celadon glaze batching weight percent composition: Linggen glaze soil 48%, limestone 8.8%, quartz 9%, Dayao Zijin soil (place of origin: Dayao Village, Xiaomei Town, Longquan City, Zhejiang Province) 18%, West Source glazed soil (origin: Yuandi Village, Shangyang Town, Longquan City, Zhejiang Province) 15%, fluorite 1.2%, all kinds of raw materials are refined and selected according to the formula requirements and mixed evenly. The ball stone: glaze: water is about 2 : 1: 0.6 put into the ball milling equipment, after 18 hours of ball milling to a fineness of 120 mesh, filter it into a glaze slurry and then use it for later use.

[0022] Embodiment Longquan Ming Dynasty official kiln celadon clay batching weight percent composition: Dayao Zijin soil (place of origin: Dayao Village, Xiaomei Town, Longquan City, Zhejiang Province) 15%, kaolin 5%, Hengtan porcelain clay (place of origin: Shangyang, Longquan City, Zhejiang Provi...

Embodiment 2

[0026] Embodiment Longquan Ming Dynasty official kiln celadon glaze material is composed in percentage by weight of ingredients: Linggen glaze soil 47%, limestone 9%, quartz 9%, Dayao Baoxi Zijin soil (place of origin: Dayao Village, Xiaomei Town, Longquan City, Zhejiang Province) 15.5%, Xiyuan Glazed Soil (origin: Yuandi Village, Shangyang Town, Longquan City, Zhejiang Province) 18%, fluorite 1.5%; all kinds of raw materials are finely selected according to the formula and mixed evenly, using ball stone: glaze: The water is about 2:1:0.6 into the ball milling equipment, and after 18 hours of ball milling, the fineness is 120 mesh, and it can be filtered into glaze slurry.

[0027]Embodiment Longquan official kiln celadon clay batching weight percentage composition in Ming Dynasty: Dayao Zijin soil (place of origin: Dayao Village, Xiaomei Town, Longquan City, Zhejiang Province) 15%, kaolin 5%, Hengtan porcelain clay (place of origin: upper part of Longquan City, Zhejiang Provin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a Longquan official ware celadon glaze of the Ming Dynasty, wherein the glaze material comprises the following components in percentage by weight: 43-48% of Linggeng glaze clay, 6-9% of lime stone, 6-9% of quartz, 14-18% of Dayao violet gold clay, 15-22% of Xiyuan glaze clay and 1.2-1.6% of fluorite. The glaze material has green and tender glaze color as jades, moist color and luster, strong jade texture, wide adaptability and good thermal stability. The invention further provides a method for manufacturing a Longquan official ware celadon product of the Ming Dynasty by using the Longquan official ware celadon glaze of the Ming Dynasty. The method is scientific and reasonable, is easily implemented, and has high rate of finished products and good porcelain texture.

Description

technical field [0001] The invention relates to the field of ceramic arts and crafts, in particular to a Longquan Ming Dynasty official kiln celadon glaze and a method for making Longquan Ming Dynasty official kiln celadon products with the glaze. Background technique [0002] Longquan Celadon is traditionally known as "Ge Kiln" and "Dr. Kiln". Ge Kiln, Guan, Ru, Ding, and Jun were also known as the five famous kilns in the Song Dynasty. According to textual research, it was fired from the beginning of the Tang and Five Dynasties to the end of the Qing Dynasty. With a history of more than 1,600 years, it is the longest porcelain kiln system in China. In 2007, a large number of Longquan celadon from my country's "Nanhai No. 1" maritime archeology came out and a large number of Longquan celadon collected by world-renowned museums were sold all over the world with its jasper-like glaze color, simple and elegant shape, smooth and beautiful lines and utensils for both refined an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/86
Inventor 李邦强陈华
Owner 李邦强
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products