A kind of 440c stainless bearing steel grain refiner and preparation method thereof

A technology of grain refiner and bearing steel, which is applied in the field of grain refinement of metal materials, can solve the problems of large energy consumption, raw material oxidation, loss, etc.

Active Publication Date: 2022-05-27
NORTHEASTERN UNIV LIAONING
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Under such high temperature conditions, it will not only consume a lot of energy to raise the temperature, but also inevitably oxidize the raw materials, resulting in a certain loss
In addition, at the temperature of steelmaking, magnesium is very easy to gasify and quickly floats to the surface of molten steel, and it is difficult to play its role in refining grains.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of 440c stainless bearing steel grain refiner and preparation method thereof
  • A kind of 440c stainless bearing steel grain refiner and preparation method thereof
  • A kind of 440c stainless bearing steel grain refiner and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0022] Take the tempered 440C stainless bearing steel with grain refining agent added, wherein the grain refining agent is 0.2% of the total mass of the 440C stainless bearing steel, and its chemical composition (mass fraction wt%) is: C: 1.02, Si: 0.45, Mn: 0.4, Cr: 18.03, Ni: 0.57, Mo: 0.53, Mg: 0.0029, and the rest are Fe. Its grain size is shown in Table 1.

example 2

[0024] Take the tempered state 440C stainless bearing steel with grain refining agent, wherein the grain refining agent is 0.4% of the total mass of the 440C stainless steel bearing steel, and its chemical composition (mass fraction wt%) is: C: 1.04, Si: 0.46, Mn: 0.4, Cr: 18.49, Ni: 0.61, Mo: 0.54, Mg: 0.0081, and the rest are Fe. Its grain size is shown in Table 1.

example 3

[0026]Take the tempered 440C stainless bearing steel with grain refining agent, wherein the grain refining agent is 0.6% of the total mass of the 440C stainless steel bearing steel, and its chemical composition (mass fraction wt%) is: C: 1.00, Si: 0.45, Mn: 0.4, Cr: 17.84, Ni: 0.59, Mo: 0.53, Mg: 0.0160, and the rest are Fe. Its grain size is shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
purityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a 440C stainless bearing steel grain refiner and a preparation method thereof. The 440C stainless bearing steel grain refiner includes Mg powder, Fe powder and nano C powder, and the Fe powder, Mg powder and nano The mass ratio of C powder is 93.9-94.1:4.9-5.1:0.9-1.1. The 440C stainless bearing steel grain refiner provided by the present invention effectively avoids the adhesion of Mg in the compressed refiner through the nano-C powder therein, and at the same time, the nano-C powder reacts with the oxygen in the molten steel to generate The fine CO bubbles can make the Mg particles quickly break away from the block refiner, so that the magnesium is evenly distributed in the molten steel. During the solidification process of molten steel, magnesium will segregate at the grain boundary to fill the surface defects of the grain boundary, thereby reducing the surface tension on the two-phase interface, increasing the nucleation speed, reducing the grain boundary energy and reducing the grain boundary energy. The driving force of grain growth limits the growth of grains and improves the strength and toughness of 440C stainless bearing steel.

Description

Technical field [0001] The present invention belongs to the field of grain refinement technology for metal materials, involving a grain refining agent for 440C stainless steel bearing steel. Background [0002] As a stainless steel bearing steel, 440C has a carbon content of 1.0% and a chromium content of 16% to 18%. It is mainly used for the manufacture of bearing parts working in corrosive environments and lubrication-free strong oxidation atmospheres. 440C has good high temperature dimensional stability, so it can also be used as a corrosion-resistant high temperature bearing steel. In addition, it can also be used to manufacture high-quality knives, such as medical scalpels, scissors, etc. Bearings are subjected to extremely high pressure and friction during operation, so 440C bearing steels are required to have high and uniform hardness and wear resistance, as well as high elastic limits. The requirements for the uniformity of the chemical composition of the bearing steel, t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C21C7/00C22C38/04C22C38/02C22C38/44
CPCC21C7/0006C21C7/0037C22C38/04C22C38/02C22C38/44C22C38/002
Inventor 李阳杨皓李花兵孙深孙萌姜周华陈常勇李立业王琪王琦
Owner NORTHEASTERN UNIV LIAONING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap