A kind of halogen-free environment-friendly EPDM rubber/negative oxygen ion powder blended closed-cell secondary foaming material and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of EPDM rubber and negative oxygen ion powder is applied in the field of foaming materials, which can solve the problems of poor dispersion, affect quality, fail to improve the air quality of the surrounding environment and benefit physical and mental health, and achieve a synchronous dispersion rate. Effect
Active Publication Date: 2020-08-28
YIBAO FUJIAN POLYMER MATERIALS
View PDF3 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Plastics, rubber, and rubber products containing tourmaline PHR and tender shale (negative oxygen ion powder) produced according to the aforementioned technology can be widely used in sporting goods, medical protective gear, dining utensils, office supplies, automotive interiors, decorations Materials and other products, when people use and touch such products, these products will exert the characteristics of tourmaline and tender shale (negative oxygen ion characteristics), can purify the surrounding environment and water quality, release negative oxygen ions, stimulate cell activity, and promote plant growth. Growth and development, prevention of electromagnetic radiation, etc., make people benefit from it. However, due to the material differences between rubber materials and tourmaline powder and tender shale, and tourmaline powder and tender shale also have high biological activity, for foaming materials It is difficult to say that the poor dispersion after processing and integration is difficult. If tourmaline powder and tender shale cannot be effectively and evenly dispersed in rubber molecules to form clusters, it will not only affect the quality of rubber products, but also cannot fully release a sufficient amount of negative energy. Oxygen ions cannot give full play to the effect of air energy negative oxygen ion powder, and the concentration of negative oxygen ions released by the product cannot reach 200-400 per cubic centimeter in static state and 400-1000 per cubic centimeter in dynamic state, and there is no improvement The air quality of the surrounding environment and the original intention of being beneficial to physical and mental health, therefore, how to improve the dispersion of negative oxygen ion powder in rubber, reduce costs, and improve the comprehensive physical properties of products, so as to enhance the application range of ecological health is an urgent need to solve in the field of foaming material technology important technical issues
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0065] A method for preparing a halogen-free environment-friendly EPDM rubber / negative oxygen ion powder blended closed-cell secondary foaming material, comprising the following steps:
[0066] (1) Preparation of negative oxygen ion premixed powder: put 100PHR tourmaline powder, 100PHR wizard R series plastic / rubber additive 1250 mesh, 5PHR chelating titanate coupling agent, and 30PHR magnesium strong powder into Φ800 *1000mm high-speed mixing tank, stirring for 12 minutes, continuously controlling the temperature at 80°C±5°C during the stirring process, and obtaining the negative oxygen ion premixed powder after stirring, and weighing the negative oxygen ion premixed powder according to the formula weight PHR repackage;
[0067] (2) Internal mixing: a. Mix 100PHR of EPDM rubber, 35PHR of negative oxygen ion premixed powder, 30PHR of carbon black, 1.5PHR of anti-fogging agent, 2PHR of anti-aging agent, and 1.5PHR of antioxidant , the dispersant of 1.5PHR, the flow agent of 1P...
Embodiment 2
[0086] The preparation method of the EPDM / PP / TPE / negative oxygen ion powder blended closed-cell secondary foaming material described in Example 2 is completely consistent with Example 1, the difference is that the proportions of the components in Example 2 are as follows:
[0087] EPDM 100PHR;
[0088] Negative oxygen ion premixed powder 45PHR;
[0089] Carbon black 25PHR;
[0090] Softener 28PHR;
[0091] Antifogging agent 1.5PHR;
[0092] Antiaging agent 2PHR;
[0093] Antioxidant 1.5PHR;
[0094] Dispersant 2PHR;
[0095] Flow agent 1PHR;
[0096] Plasticizer 1.2PHR;
[0097] Vulcanizing agent 2PHR;
[0098] Accelerator 2.6PHR;
[0099] Foaming agent 4.6PHR;
[0100] Foaming aid 5PHR;
[0101] The physical properties of the halogen-free environment-friendly EPDM rubber / negative oxygen ion powder blended closed-cell secondary foaming material prepared in Example 2 are shown in Table 4 below:
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to the technical field of foaming materials and provides a halogen-free and environment-friendly EPDM (Ethylene-Propylene-Diene Monomer) rubber / negative oxygen ion powder mixed closed-cell secondary foaming material and a preparation method thereof. Negative oxygen ion powder of the halogen-free and environment-friendly EPDM rubber / negative oxygen ion powder mixed closed-cell secondary foaming material can be effectively combined with halogen-free and environment-friendly EPDM rubber under the condition that high biological activity of the negative oxygen ion powder is maintained, the dispersity of the negative oxygen ion powder on rubber molecules is effectively improved, original excellent physical properties of the rubber can be effectively reserved, enough negative oxygen ions can be released effectively and sufficiently, a product prepared from the secondary foaming material can continuously release 1,500 negative oxygen ions in each cubic centimeter of space in a static state, can improve ambient air quality and benefits human health; the preparation method of the halogen-free and environment-friendly EPDM rubber / negative oxygen ion powder mixed closed-cell secondary foaming material is simple to operate, easy to implement and suitable for large-scale production.
Description
technical field [0001] The invention relates to a foaming material, in particular to a halogen-free environment-friendly EPDM rubber / negative oxygen ion powder blended closed-cell secondary foaming material and a preparation method thereof. Background technique [0002] In recent years, EPDM foaming materials have been widely used in important industries of the national economy such as automobiles, electronics, electrical appliances, and construction. At the same time, due to the tensile strength of EPDM foaming materials in many fields in the industry , Elongation at break, tear strength, high temperature resistance and other properties have higher requirements, and the odor of EPDM foam materials is relatively heavy, most of which contain halogens (fluorine, chlorine, bromine, iodine), halogens in materials (fluorine, chlorine, bromine, iodine) foaming materials made of more than a certain value will produce a hydrogen halide gas when burned, which will cause suffocation o...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more