Renewable-aggregate industrial mortar and preparation method thereof

A technology for regenerating aggregates and mortar, applied in the field of industrial mortar, can solve problems such as affecting application and insufficient mortar strength, and achieve the effects of avoiding pollution, increasing added value, and realizing industrial scale development.

Inactive Publication Date: 2013-12-04
LANGFANG RONGSHENG CONCRETE
View PDF1 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Although prior art CN101343160A (disclosure date January 14, 2009) also discloses a kind of concrete recycled aggregate industrial mortar and its preparation method, this prior art pays too much attention to thermal insulation performance, and the strength of prepared mortar is not enough, which affects its Application in actual production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Production of recycled aggregate floor plastering insulation mortar. (1) To prepare floor mortar aggregates, according to the preparation process of recycled concrete aggregates, regenerate concrete into concrete recycled aggregates with a particle size of ≤5mm. (2) Formula: 20% Portland cement, 15% lime, 12% concrete recycled aggregate with particle size ≤ 5mm, 7% clay brick recycled aggregate with particle size ≤ 5mm, glass recycled aggregate with particle size ≤ 5mm 2.5%, 15% natural yellow sand, 20% fly ash, 7% water reducing agent and appropriate amount of water. Among them, the water reducing agent requires a water reducing rate greater than 12%. (3) Manufactured according to the production process of recycled aggregate industrial mortar. Uses: Mainly used for floor plastering of residential rooms, parlors, and public civil buildings.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an industrial mortar using renewable aggregates as a main filling raw material and a preparation method of the industrial mortar. The production formula of the industrial mortar is that 10-30 percent of silicate cement, 10-20 percent of calcium oxide, 10-15 percent of renewable concrete aggregate of which particle size is smaller than or equal to 5 mm, 5-10 percent of renewable clay brick aggregate of which particle size is smaller than or equal to 5 mm, 2-3 percent of renewable glass aggregate of which particle size is smaller than or equal to 5 mm, 10-20 percent of natural yellow sand, 15-25 percent of coal ash, 4-6 percent of water-reducing agent and a proper quantity of water are adopted, wherein the water-reducing rate of the water-reducing agent is required to be greater than 12 percent; preferably, the formula does not contain other components. Through the process of the method, the cost is effectively reduced; the mortar can be used in building surfaces and wall surfaces for plastering, is conducive to improving thermal insulation performance and energy-saving level of buildings, and has higher pressure resistance and tensile strength compared with existing similar products.

Description

technical field [0001] The invention relates to an industrial mortar made of recycled aggregates, which has the characteristics of ecological environment protection and the advantages of heat preservation function. Background technique [0002] For a long time, construction waste with mineralization characteristics has not been well utilized as a resource in our country. Existing construction waste bricks and construction waste block technologies are extensive use of construction waste "currency", the products have no characteristics, and the technology lacks innovation, so the market rate of return is low. The scientific utilization of construction waste slag resources is classified utilization, and the different material properties of different construction waste slags are fully utilized to produce building materials with outstanding functions. [0003] my country's construction waste is mainly composed of waste concrete and waste bricks (walls), followed by a small amoun...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/04C04B18/08
CPCY02W30/91
Inventor 刘进辉施学涛
Owner LANGFANG RONGSHENG CONCRETE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products