Dispersion strengthening platinum/rhodium30-platinum/rhodium6 thermocouple wires and production method thereof

A technology of dispersion strengthening and thermocouple wire, which is applied in the direction of directly heat-sensitive electric/magnetic element thermometers, measuring heat, and using electric devices, etc., which can solve the problems of high investment and use costs, poor anti-pollution ability, and long service life. Limited and other problems, to achieve the effect of stable thermoelectric potential, strong creep resistance, and thin diameter

Active Publication Date: 2011-04-20
英特派铂业股份有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Thermocouple wire is used to make various temperature measuring elements, and is widely used in temperature measurement in various fields such as steel industry and glass industry. Platinum rhodium is widely used in the prior art 30 -platinum rhodium 6 Thermocouple wire, its positive platinum rhodium 30 The nominal composition is rhodium Rh30%, platinum Pt is the balance, negative platinum rhodium 6 The nominal composition is rhodium Rh6%, and platinum Pt is the balance. This kind of thermocouple can measure temperature in the temperature range of 1100-1700 °C, and can be used under high-temperature oxidation conditions, but platinum-rhodium 6 The crystal grains are easy to coarsen, and the anti-pollution ability is poor, causing thermal potential instability, limited service life, high investment and use costs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Embodiment 1: Pt 94.0%, Rh 6.0%.

[0029] Technical performance: the fracture life of ordinary platinum rhodium when subjected to the same stress at high temperature 6 Even wires are equivalent; for each roll of even wires, when the reference end temperature is 0°C, the thermal electromotive force measured at different test temperatures meets the requirements of GB / T 2902.

Embodiment 2

[0030] Embodiment 2: Pt93.812%, Rh5.988%, Zr0.1%, Ca0.1%.

[0031] Technical performance: when subjected to the same stress at high temperature, the fracture life is as long as that of ordinary platinum rhodium 6 About 20 times that of even wire; for each roll of even wire, when the reference end temperature is 0°C, the thermal electromotive force measured at different test temperatures meets the requirements of GB / T2902.

Embodiment 3

[0032] Example 3: Pt 93.624%, Rh 5.976%, Zr 0.2%, La 0.2%.

[0033] Technical performance: when subjected to the same stress at high temperature, the fracture life is as long as that of ordinary platinum rhodium 6 About 15 times that of even wire; for each roll of even wire, when the reference end temperature is 0°C, the thermal electromotive force measured at different test temperatures meets the requirements of GB / T2902.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses dispersion strengthening platinum / rhodium30-platinum / rhodium6 thermocouple wires, comprising a cathode and an anode; the thermocouple wires are characterized in that the anode contains ingredients according to the following weight percentage: 30% of rhodium; the excess is platinum; the cathode contains ingredients according to the following weight percentage: 5.94-6% of rhodium; 0-0.5% of zirconium; 0-0.5% of yttrium; 0-0.5% of calcium; 0-0.5% of lanthanum; 0-0.5% of titanium; the excess is platinum. The production method of dispersion strengthening platinum / rhodium30-platinum / rhodium6 thermocouple wires comprise mixing ingredients, vacuum melting, placing and rolling, oxidizing, combined machining and drawing forming. The dispersion strengthening platinum / rhodium30-platinum / rhodium6 thermocouple wires of the invention enjoy long service life, high adaptive temperature, strong contamination resistance and low use cost.

Description

technical field [0001] The invention belongs to the technical field of metal materials, in particular to a dispersion strengthened platinum rhodium 30 -platinum rhodium 6 Thermocouple wire and its production method. Background technique [0002] Thermocouple wire is used to make various temperature measuring elements, and is widely used in temperature measurement in various fields such as steel industry and glass industry. Platinum rhodium is widely used in the prior art 30 -platinum rhodium 6 Thermocouple wire, its positive platinum rhodium 30 The nominal composition is rhodium Rh30%, platinum Pt is the balance, negative platinum rhodium 6 The nominal composition is rhodium Rh6%, and platinum Pt is the balance. This kind of thermocouple can measure temperature in the temperature range of 1100-1700 °C, and can be used under high-temperature oxidation conditions, but platinum-rhodium 6 The crystal grains are easy to coarsen, and the anti-pollution ability is poor, causin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G01K7/02C22C5/04C22C1/02
Inventor 蒋正荣尹俊
Owner 英特派铂业股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com