A kind of asphalt pavement stress reflection crack repair material and repair method

A technology for reflecting cracks and asphalt pavement, applied in building insulation materials, roads, roads, etc., can solve problems such as poor flow permeability, high viscosity of modified asphalt, secondary damage, etc., to improve stability, enhance penetration, and improve The effect of high temperature stability

Active Publication Date: 2018-02-09
CHINA PETROLEUM & CHEM CORP +1
View PDF11 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Modified asphalt is used as the repair material. If the joint filling process without slotting is used for repairing, due to the high viscosity of the modified asphalt and poor flow and permeability, the asphalt poured into the cracks in the road surface is very little. Therefore, the slotting process is generally used, but It is only the modified asphalt that fills the gaps in the asphalt pavement surface layer, and the cracks in the base layer still exist, which is a temporary solution, not a permanent cure
In addition, during the process of slotting with a slotting machine, secondary damage will be caused to the small cracks at the edge of the crack. Even if the cracks are filled and sealed, rainwater will still enter from the small cracks at the edge of the crack, causing the potting glue to fail.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of asphalt pavement stress reflection crack repair material and repair method
  • A kind of asphalt pavement stress reflection crack repair material and repair method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] (1) Mix No. 93 gasoline, aviation kerosene and No. 0 diesel oil according to the mass ratio of 2:1:0.4 to prepare diluent for use.

[0055] (2) Zhenhai SBS modified asphalt (60%) with a penetration degree (25°C, 0.1mm) of 61, stop heating after heating to 140°C, and add alkyl polyoxyethylene ether (4%) under stirring 5 minutes. Finally, add the configured diluent (36%) and stir for 15 minutes to obtain the high-permeability liquid asphalt of the present invention.

Embodiment 2

[0057] (1) Mix No. 93 gasoline, aviation kerosene and No. 0 diesel oil according to the mass ratio of 1.5:1:0.4 and prepare it as a diluent for use.

[0058] (2) Heat the Zhenhai Grade A bitumen (70%) with a penetration (25°C, 0.1mm) of 61 to 120°C, stop heating, add the prepared diluent (28%) while stirring, and stir for 5 minutes. Finally, add fatty alcohol polyoxyethylene ether (2%) and continue stirring for 20 minutes to obtain the high-permeability liquid pitch of the present invention.

[0059] Filling glue:

Embodiment 3

[0061] (1) Heat Zhenhai base asphalt (83%) with a penetration degree (25°C) of 110 to 180°C-190°C, add 60 mesh waste tire rubber powder (16%), and perform high-shear grinding for 2-3 times Stir in the development tank for 1 h,

[0062] (2) Add 1% slow-release chemical modifier (benzoyl peroxide), stir evenly, and then inject compressed air from the bottom of the tank. Air volume is 0.2 m 3 × kg -1 × h -1 . Stirring was continued for 1 hour, after which the blowing of compressed air was stopped.

[0063] (3) Add an equal amount of SBS modified asphalt (SBS content: 6%, penetration (25°C): 70 1 / 10mm) and continue stirring for 1 hour. Promptly obtain the caulking glue of the present invention.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
penetrationaaaaaaaaaa
penetrationaaaaaaaaaa
penetrationaaaaaaaaaa
Login to View More

Abstract

The invention discloses an asphalt pavement stress reflection crack repair material and a crack repair method using the material. The repair materials are high-permeability liquid asphalt and high-performance joint glue. Among them, the joint glue is a composite modified material containing rubber asphalt and polymer modified asphalt. During the preparation of rubber asphalt, slow-release chemical modifiers and oxygen are blown in to increase and improve the rubber powder in the rubber asphalt. Stability in hot asphalt, and then add a certain proportion of SBS or SBR modified asphalt with high polymer content to rubber asphalt, so that the joint glue of the present invention not only has the advantages of SBS modified asphalt, but also has the advantages of rubber powder asphalt Features, with excellent high temperature stability, anti-aging performance, low temperature cracking resistance, fatigue resistance and interface bonding performance.

Description

technical field [0001] The invention relates to a pavement repair material and a repair method, belonging to the technical field of road maintenance. In particular, it relates to a material and a repairing method which are convenient and fast in construction and fundamentally and effectively repair the stress reflection cracks of the asphalt pavement. Background technique [0002] With the development of the national economy, the mileage of high-grade highways continues to increase. In order to meet the requirements of heavy traffic and heavy load on high-grade highways, the semi-rigid pavement with inorganic binder stabilized soil as the base layer and asphalt concrete as the surface layer is widely used in high-grade pavements. However, it has been found to have serious problems after long-term use. crack problem. For the semi-rigid base asphalt pavement, the semi-rigid base will shrink and crack under the temperature gradient and humidity changes, and then reflect upwar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L95/00E01C11/00
Inventor 张建峰郭皎河刘树华傅丽姚汉荣
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com