CSM composite hose and production method thereof

A composite hose and rubber technology, applied in the CSM composite hose and its production field, can solve the problems of poor bonding firmness, separation of the two rubber materials, and difficulty in bonding the two rubber materials, and achieve good heat resistance and oil resistance. performance effect

Inactive Publication Date: 2015-07-08
ZHEJIANG JIUYUN VEHICLE PARTS
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The fuel filler hose of existing diesel vehicles uses NBR rubber hose internally and CSM composite rubber hose for outsourcing. However, due to the defects of the existing formula of the two rubber materials, it is difficult to bond the two rubber materials, and the bonding strength is poor.
In the process of use, it is easy for the two rubber materials to separate, which will cause the safety of diesel vehicles.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] The formula of the CSM composite rubber hose described in this embodiment is composed of nitrile rubber, CSM, carbon black, calcium hydroxide, magnesium oxide, acid absorbing agent, rubber release agent, plasticizer, anti-aging agent, triallyl iso Composed of cyanurate and vulcanizing agent, wherein the mass parts of each component are: 45 parts of nitrile rubber, 55 parts of CSM, 72 parts of carbon black, 3 parts of calcium hydroxide, 4 parts of magnesium oxide, 4 parts of acid absorbing agent , 2 parts of rubber release agents, 25 parts of plasticizers, 3 parts of antioxidants, 1 part of triallyl isocyanurate, 2 parts of vulcanizing agents; the described nitrile rubber is 230 nitrile rubber, carbon black It is N774, rubber release agent is WB222, plasticizer is TOTM, anti-aging agent is BLE, vulcanizer is HVA-2.

[0011] A kind of production method of CSM composite rubber hose, according to formula quantity weighs each raw material in proportion; First put nitrile rub...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of automobile hoses and particularly relates to a CSM composite hose. The CSM composite hose comprises the following components in parts by mass: 45 parts of nitrile rubber, 55 parts of CSM, 72 parts of carbon black, 3 parts of calcium hydroxide, 4 parts of magnesium oxide, 4 parts of an acid acceptor, 2 parts of a rubber releasing agent, 25 parts of a plasticizer, 3 parts of an antiager, 1 part of triallyl isocyanurate and 2 parts of a vulcanizing agent. According to the CSM composite hose and a production method thereof, the hose produced according to the method is vulcanized for 20min at 170 DEG C; after the hose is aged in hot air at 120 DEG C for 70h, the hardness change value is 3 degrees, the intensity change value is +11%, and the elongation change value is -14%; and after the hose in immersed in NO.3 oil at 120 DEG C for 70h, the volume change value is +58%. Therefore, the CSM composite hose has favorable heat resistance and oil resistance.

Description

technical field [0001] The invention relates to the field of rubber hoses for vehicles, in particular to a CSM composite rubber hose and a production method thereof. Background technique [0002] The fuel filler hose of existing diesel vehicles uses NBR rubber hose inside and CSM composite rubber hose for outsourcing. However, due to the defects of the existing formula of the two rubber materials, it is difficult to bond the two rubber materials, and the bonding firmness is poor. In the process of use, it is easy for the two rubber materials to separate, which will cause the safety of diesel vehicles. Contents of the invention [0003] The object of the present invention is to provide a kind of CSM composite rubber hose and its production method in order to solve the deficiency of above-mentioned technology, the CSM rubber hose and NBR rubber hose produced by this method are well bonded, and the firmness of bonding is high. [0004] In order to achieve the above object, t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L23/34C08L9/02C08K13/02C08K3/04C08K3/22C08K5/3492
CPCC08L23/34C08L2201/08C08L2203/18C08L2312/00C08L9/02C08K13/02C08K3/04C08K2003/2206C08K2003/222C08K5/34924
Inventor 王平闻浩泉张利芳
Owner ZHEJIANG JIUYUN VEHICLE PARTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com